Metal–organic framework (MOF)-based electrical impedance sensors are a growing class of sensors that show utility in the detection of environmentally toxic gases. Detection of trace NH 3 has been particularly difficult to design due to the low electrical response of NH 3 . However, this has been circumvented by judiciously selecting a MOF that has enhanced electrical response to NH 3 due to coadsorption with predominant atmospheric gases such as water. Herein, an MOF Cu(cyhdc) based sensor has been successfully demonstrated for the enhanced detection of environmentally toxic NH 3 gas. The sensor shows a change in impedance when it is exposed to 5 ppm of NH 3 . At 20 °C, >30% relative humidity (RH) is necessary to elicit a change, with the response increasing with RH and reaching 3170× at 92% RH, producing the largest published response to NH 3 for a MOF direct electrical sensor. In the absence of water, no change is observed toward 5 ppm of NH 3 over 20–50 °C. Here, this electrical response is largely driven by huge decreases in the imaginary component of the impedance, attributed to increased capacitance at the surface of the MOF crystallites upon NH 3 and H 2 O coadsorption. Complementary structural and microstructural characterization proves that the Cu(cyhdc) crystalline structure and morphology remain intact under trace NH 3 and/or H 2 O adsorption. Despite extremely low NH 3 , loadings seen in TGA, XPS, and FT-IR confirm NH 3 and H 2 O adsorption, and changes to the metal-carboxylate IR peak positions are observed upon NH 3 adsorption. Concentrated primarily at the outer surfaces of the MOF crystallites, this NH 3 and H 2 O coadsorption effectively increases the surface capacitance across the Cu(cyhdc) powder and enables direct electrical detection of trace NH 3 . Together, these results demonstrate how coadsorption of specific molecules (H 2 O) can be used to enable the electrical detection of trace toxic gases that would otherwise not have produced a MOF sensor response.