Experimental and Numerical Analysis of Triaxially Braided Composites Utilizing a Modified Subcell Modeling Approach

Cater, Christopher·Xiao, Xinran·Goldberg, Robert K.·Kohlman, Lee W.
View original source ↗Export metadata ↓

Abstract

A combined experimental and analytical approach was performed for characterizing and modeling triaxially braided composites with a modified subcell modeling strategy. Tensile coupon tests were conducted on a [0deg/60deg/-60deg] braided composite at angles of 0deg, 30deg, 45deg, 60deg and 90deg relative to the axial tow of the braid. It was found that measured coupon strength varied significantly with the angle of the applied load and each coupon direction exhibited unique final failures. The subcell modeling approach implemented into the finite element software LS-DYNA was used to simulate the various tensile coupon test angles. The modeling approach was successful in predicting both the coupon strength and reported failure mode for the 0deg, 30deg and 60deg loading directions. The model over-predicted the strength in the 90deg direction; however, the experimental results show a strong influence of free edge effects on damage initiation and failure. In the absence of these local free edge effects, the subcell modeling approach showed promise as a viable and computationally efficient analysis tool for triaxially braided composite structures. Future work will focus on validation of the approach for predicting the impact response of the braided composite against flat panel impact tests.

Explore related subjects

MicromechanicsPolymer Matrix CompositesImpact

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Cater, Christopher, Xiao, Xinran, Goldberg, Robert K., Kohlman, Lee W.. 2015-09-28. Experimental and Numerical Analysis of Triaxially Braided Composites Utilizing a Modified Subcell Modeling Approach. https://ntrs.nasa.gov/citations/20150023035

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

NASA NTRS2026

Micromechanical Design of Carbon Nanotube Ribbon Reinforced Polymer Composite Materials

Lightweight materials are an important component of the design of aerospace structures. Carbon nanotube materials have been considered for this purpose due to the strength and stiffness of individual nanotubes, and the commercial availability of bulk formats such as fibers. These fibers can have a ribbon cross section which results in a different design space for their composites relative to traditional reinforcements which have a round cross section. This work applies brick-and-mortar micromechanical models and classical lamination theory with an inverse approach to investigate the design space of these composites. Using this approach, the influences of fiber geometry and axial and transverse mechanical properties are mapped. Finally, a sensitivity study is performed and the relative impacts of ±10% variations in the constituent material and geometric properties are ranked. Lamina axial moduli were found to range from a maximum of 3x to 1x minimum relative to a target quasi-isotropic laminate modulus depending on the anisotropy and shear modulus of the lamina. The fiber targets depended strongly on the fiber volume fraction in the lamina and the fiber axial modulus target was found to range from 4.8x to 3.2x the quasi-isotropic laminate target. The sensitivity analysis found that the largest driver of performance was the volume fraction, followed by the fiber axial modulus. While bio-based brick-and-mortar composites, such as nacre, can benefit from reinforcement aspect ratios above 10, for carbon nanotube ribbon (or carbon fiber)/polymer composites the sensitivity study indicated that the optimal cross-sectional aspect ratio was relatively smaller, potentially less than three.

Micromechanics↗
NASA NTRS2024

Analytical Simulation of Effects of Local Mechanisms and Microstructure on Creep Response of Unidirectional Ceramic Matrix Composites

A micromechanics-based method has been developed to analyze the creep response of uncoated ceramic matrix minicomposites. Although the global stress level at which the creep response is analyzed is lower than the composite proportional limit, local stresses are assumed to be high enough that localized damage is present in the composite in the form of matrix microcracks. To model the composite creep response, including the effects of matrix cracking, a fiber shear lag-based methodology is employed. In this approach, stresses are assumed to vary in the fiber as a function of time and distance from the crack plane. The varying stresses are then used to compute the overall creep strain for the composite. Various assumptions regarding the level of matrix microcracking in the composite and the level of creep in the fiber and matrix in various portions of the composite unit cell are also examined. The creep response of the fiber is modeled using a linear Burgers model. The model is applied to a SiCf/SiC unidirectional minicomposite system. The computed creep results are compared to experimentally obtained values. The effects of the local fiber volume fraction on the overall creep response of the composite are also studied. This work will allow increased understanding of the key material damage mechanisms and load sharing that take place during creep conditions and can be expanded to provide improved analysis methods for full macrocomposites.

Micromechanics↗
NASA NTRS2024

Analytical Simulation of the Effects of Local Mechanisms and Microstructure on the Creep Response of Unidirectional Ceramic Matrix Composites

A micromechanics-based method has been developed to analyze the creep response of uncoated ceramic matrix minicomposites. Although the global stress level at which the creep response is analyzed is lower than the composite proportional limit, local stresses are assumed to be high enough that localized damage is present in the composite in the form of matrix microcracks. To model the composite creep response including the effects of matrix cracking, a fiber shear lag-based methodology is employed. In this approach, stresses are assumed to vary in the fiber as a function of time and distance from the crack plane. The varying stresses are then used to compute the overall creep strain for the composite. Various assumptions regarding the level of matrix microcracking in the composite, and the level of creep in the fiber and matrix in various portions of the composite unit cell, are also examined. The creep response of the fiber is modeled using a linear Burgers model. The model is applied to a SiC f /SiC unidirectional minicomposite system. The computed creep results are compared to experimentally obtained values. The effects of the local fiber volume fraction on the overall creep response of the composite are also studied. This work will allow increased understanding of the key material damage mechanisms and load sharing that take place during creep conditions and can be expanded to provide improved analysis methods for full macrocomposites.

Micromechanics↗