Smart Coatings for Corrosion Protection

Calle, Luz Marina·Li, Wendy·Buhrow, Jerry W.·Johnsey, Marissa N.
View original source ↗Export metadata ↓

Abstract

Nearly all metals and their alloys are subject to corrosion that causes them to lose their structural integrity or other critical functionality. It is essential to detect corrosion when it occurs, and preferably at its early stage, so that action can be taken to avoid structural damage or loss of function. Protective coatings are the most commonly used method of corrosion control. However, progressively stricter environmental regulations have resulted in the ban of many commercially available corrosion protective coatings due to the harmful effects of their solvents or corrosion inhibitors. This work concerns the development of a multifunctional, smart coating for the autonomous control of corrosion. This coating is being developed to have the inherent ability to detect the chemical changes associated with the onset of corrosion and respond autonomously to indicate it and control it.

Explore related subjects

CoatingsCorrosion ControlCorrosion

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Calle, Luz Marina, Li, Wendy, Buhrow, Jerry W., Johnsey, Marissa N.. 2016-11-14. Smart Coatings for Corrosion Protection. https://ntrs.nasa.gov/citations/20160013624

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2023

Cladding and Butt-Joining Dissimilar Aluminum Alloys Simultaneously via Shear Assisted Processing and Extrusion

Shear assisted processing and extrusion has been used to fabricate multi-metallic tubing that incorporates regions with clad and butt-joined structures. In this work, aluminum alloys 6061, 7075, and 1100 are combined to create a monolithic extruded tubing with weldable ends (6061), a high strength center (7075), and a corrosion-resistant cladding (1100). Optical microscopy shows a gradual, defect-free, transition between alloys at the butt-joint interfaces and a sharp transition between alloys at the clad interface. Tensile testing proved the mechanical coherency of the joint, with failure occurring outside the tri-metallic structure. In conclusion, smoothed particle hydrodynamic simulations identified a spiral pattern of the cladding alloy that leads to inconsistent cladding thickness, and identified a simplified 2-alloy combination of aluminum alloys 6082 and 2014 that accomplished the design objectives of the tri-metallic structure.

Coatings↗
NASA NTRS2021

Modeling of the Influence of Thermally Grown Oxide (TGO) Layers on the Driving Forces in Environmental Barrier Coating Systems

Environmental barrier coatings (EBC) are an enabling technology for the successful application of ceramic matrix composites (CMCs) in air-breathing gas turbine engines. EBCs are susceptible to several failure modes including oxidation/delamination, recession, chemical attack and dissolution, thermomechanical degradation, erosion, and foreign object impact damage in a combustion environment. Spallation of environmental barrier coating (EBC), induced by a thermally grown oxide (TGO) layer, is a key EBC failure mode. The TGO layer, resulting from steam oxidation, grows either from a silicon bond coat layer (if present) or from a silicon carbide (SiC) based substrate itself. The TGO layer evolves (i.e., thickness increases with time) as water vapor and oxygen gradually diffuse through the EBC, and the EBC spalls off once the TGO layer reaches some critical thickness. The critical thickness of the TGO layer for failure is in the range of 20-30 microns, with the actual value depending upon exposure temperature, microstructure, etc. Current work at NASA Glenn Research Center, under the Transformative Tools and Technology (TTT) subproject is aimed at addressing associated failure modes in EBC systems and developing robust analysis tools to aid in the design/analysis of these systems. The objective of the current work is to conduct a sensitivity study to examine the influence of uniformly and non-uniformly grown oxide layers on the associated driving forces leading to spallation of the EBC when subjected to isothermal loading. The effect of damage in the TGO layer on the resulting stress states is also assessed both in uniform and non-uniform TGO layers.

Coatings↗