CMH-17 Volume 5 Ceramic Matrix Composites

Andrulonis, Rachael; Kiser, J. Douglas; David, Kaia E.; Davies, Curtis; Ashforth, Cindy

Home/Archive/NASA NTRS

NASA NTRS · 20170008120

CMH-17 Volume 5 Ceramic Matrix Composites

Andrulonis, Rachael·Kiser, J. Douglas·David, Kaia E.·Davies, Curtis·Ashforth, Cindy

View original source ↗Export metadata ↓

Abstract

A wide range of issues must be addressed during the process of certifying CMC (ceramic matrix composite) components for use in commercial aircraft. The Composite Materials Handbook-17, Volume 5, Revision A on ceramic matrix composites has just been revised to help support FAA certification of CMCs for elevated temperature applications. The handbook supports the development and use of CMCs through publishing and maintaining proven, reliable engineering information and standards that have been thoroughly reviewed. Volume 5 contains detailed sections describing CMC materials processing, design analysis guidelines, testing procedures, and data analysis and acceptance. A review of the content of this latest revision will be presented along with a description of how CMH-17, Volume 5 could be used by the FAA (Federal Aviation Administration) and others in the future.

Explore related subjects

characterization ceramic matrix composites processing standards design testing

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

Andrulonis, Rachael, Kiser, J. Douglas, David, Kaia E., Davies, Curtis, Ashforth, Cindy. 2017-06-29. CMH-17 Volume 5 Ceramic Matrix Composites. https://ntrs.nasa.gov/citations/20170008120

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2025

FTIR analysis of unaged encapsulants

Fourier transform infrared spectroscopy (FITR) analysis (in ATR mode) of unaged encapsulants (EVA, POE, EPE) from a commercial source.

characterization↗

DOE OSTI2025

High-Resolution Computed Tomography Dataset of Mount Simon Sandstone

The Illinois Basin is a critical structure for subsurface energy related activities and their implementation in the United States. The Mount Simon Sandstone has been identified as a storage target for permanent and transient storage of fluids in the basin. Known for its exceptional thickness, depth, porosity, and sealing properties of overlying formations, this saline reservoir is crucial for long-term subsurface energy efforts. We present an extensive Computed Tomography (CT) dataset on a high porosity and permeability zone in the lower Mount Simon Sandstone available on the Energy Data eXchange® (EDX). This publicly accessible database comprises over 500 GB of high-resolution CT scans of six core samples, with resolutions ranging from 14.8 µm to 0.7 µm per pixel. The scans include both dry sandstone samples and those saturated with multiple fluids, allowing for comparative analyses across different conditions and resolutions. Coarser scans capture the bedding structure of the sandstone, while finer resolutions reveal detailed pore infill and throat characteristics. Metadata on location, depth, and saturation state enhance usability, enabling quick identification and cross-sample comparisons. By providing a robust resource for research and collaboration, the database contributes to domestic energy advancement by supporting continued progress in the use of the subsurface for energy solutions.

characterization↗

DOE OSTI2025

Exploring New Applications of Municipal Solid Waste

This study aimed to (i) characterize municipal solid waste (MSW) sourced from Utah and Michigan transfer stations and (ii) upcycle, produce, and evaluate composites derived from this MSW. Composition analysis showed that the MSW was composed of a variety of commodity plastics, paper/cardboard, and inorganic materials. Detailed chemical analysis for lignin, cellulose, hemicellulose, and lipids was performed. The plastics identified were mainly polyethylene, polypropylene, polystyrene, and poly (ethylene terephthalate). The compoundability of the MSW was assessed by torque rheometry. Composites were prepared by compounding the MSW in an extruder. A composite flexural strength of 29 MPa and a modulus of 1.0 GPa was achieved. The thermal properties of the composites were also determined. The melt flow behavior of the MSW composites at 190 °C was comparable to wood plastic composite formulations.

characterization↗