Current EBC Development and Testing at NASA

Lee, Kang·Waters, Debbie·Costa, Gustavo·Puleo, Bernadette
View original source ↗Export metadata ↓

Abstract

SiC SiC Ceramic Matrix Composites (CMCs) are a game changer for advanced power generation equipment because of their high temperature capability, oxidation resistance, and light weight that translate to significant reduction in fuel consumption and emission. Limitations of SiC SiC CMCs include surface recession and component cracking and associated chemical and physical degradation in the CMC. The solution pursued to mitigate surface recession of SiC SiC CMCs is the incorporation of coating systems that provide surface protection, which has become known as an Environmental Barrier Coating (EBC). The development of EBCs for the protection of SiC SiC CMCs was a continuation of coating development work for corrosion protection of silicon-based monolithics. The first and second generation EBCs developed in mid 1990s-early 2000s laid the foundation for current EBCs. Environmental degradation that limits EBC life includes surface recession by steam, oxidation in steam environments, and CMAS-EBC reactions. Many engine tests have been conducted since late 1990s and a first CMC component entered into service in 2016 in a commercial engine. The introduction of CMCs represents significant challenges as failure of the EBC means rapid reduction in component life. A reliable lifing method and engine-relevant testing methods to validate life need to be developed. This paper will current activities on EBC development and testing at NASA.

Explore related subjects

CMCsteam oxidationEBCrecessionwater vapor

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Lee, Kang, Waters, Debbie, Costa, Gustavo, Puleo, Bernadette. 2017-11-05. Current EBC Development and Testing at NASA. https://ntrs.nasa.gov/citations/20180004253

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

NASA NTRS2024

Hybrid Thermally Efficient Core (HyTEC) HyTEC Phase 1 – Combustor Final Report

The objective of the HyTEC – Combustor Technology project is to develop technology for a compact, low emissions, rich-burn combustor that maintains a high-level of durability. To accomplish this, the combustor will incorporate CMC liners and a CMC Dome to enable improved air utilization for mixing and NOx reduction. In particular, three technology areas were matured: metallic swirler attachment to the CMC dome, Nickel diffusion in CMC, and EBC advancements with improved durability. The maturation of these technology areas is critical to successfully designing a combustor for an engine intended to demonstrate increased thermal efficiency with integrated high-power density-core engine technologies. As part of the project, multiple swirler attachment architectures were matured through the design process, manufactured, and tested in simulated engine conditions. These architectures utilized two different approaches to attachment: a pressure loaded approach and a clamped approach. Each approach required testing at simulated engine conditions to mature the technology. These tests were developed to ensure that the probable failure mechanisms for each architecture were assessed relative to its long-term durability. After successfully testing both approaches, the pressure loaded approach was chosen based on its simplicity and its similarity to the attachment approach used on lean burn combustors. Finally, this successful testing resulted in the swirler attachment technology achieving TRL 4 status. Another aspect of concern with the metallic swirler attachment is the potential for nickel diffusion into the CMC to cause durability shortfalls. A series of tests were completed to understand both the amount of nickel that is expected to diffuse into the CMC and the effect this diffusion will have on mechanical properties of the CMC. After successfully completing this testing, the reduction in local mechanical properties was found to not have an impact on the overall durability of the CMC Dome. To further improve the overall durability, three different EBC coating architectures were also studied. One of these coatings being the current state of the art for CMC liners with the other two being proposed improvements. Coupons were produced using each coating and subjected to a series of laboratory testing. One coating was found to have an overall superior durability in laboratory testing and survived rig testing without indication of degradation. This successful testing resulted in the EBC technology achieving TRL 5 status. Overall, a design approach was successfully down-selected that achieves both the TPM requirements and the need for TRL 4+ status. This design incorporates a pressure loaded swirler attachment with an improved EBC coating (Architecture 1). This combination allows the continued use of a CMC dome and results in an improved durability for the proposed compact core combustor.

CMC↗
NASA NTRSDate not supplied

The Effect of Trailing Edge Grid Resolution in Large-Eddy Simulations

Ceramic Matrix Composite (CMC) with environmental barrier coating can tolerate significantly higher temperatures compared with the conventional metal alloy blades and thus can help achieve higher thermal efficiency in gas turbine engines. Due to the complex fabrication process of CMC blades, larger blade trailing edge thicknesses and larger leading-edge radii of curvature are expected. These features significantly alter aerodynamic performance especially near the trailing edge and thus the loss profile. In previous studies, the authors used the large eddy simulation (LES) as well as the Reynolds Averaged Navier-Stokes (RANS) coupled with an intermittency function-based transition model to simulate an aerodynamics performance of three different CMC blades and compared the predictions against the data acquired at NASA Glenn Transonic Turbine Blade Cascade Rig. Although we were able to successfully predict different characteristics of aerodynamic performance among three different blades (e.g., pressure loading and integrated losses), LES consistently predicted a small recirculation bubble at the end of the suction side. This was not inconsistent with the physics of the flow, but the pressure loading, locally, near the trailing edge, and as a result, the measured wake profiles did not match the experimental data. To delve further into these issues, a new LES grid with a much finer mesh near the trailing edge was generated where the spanwise extent of the grid was increased by 50%. An LES simulation for the CMC blade with the largest trailing edge thicknesses at the high-freestream turbulence (Tu=13%) condition showed that using such a mesh is necessary for LES to accurately capture the transition phenomena on the suction side. The resulting total pressure coefficient profile and the shift of the wake profile were greatly improved.

CMC↗