Biomass (e.g., pine sawdust, especially high–ash content pine sawdust) is commonly disposed of as waste. Combining biomass with polymers to make composite feedstocks for 3D printing has been explored as a method to reduce or repurpose the biomass waste. Although not all biocomposite properties are known, the wood-based polylactic acid (PLA) composite has promising qualities for applications in ecological settings. In this work, pine wood–PLA composite feedstock was used to 3D print supplemental roost structures for endangered tree-roosting bats, which often face a paucity of suitable naturally occurring roosts. This material combination was selected because it is estimated to degrade faster than the synthetic material systems that are used widely in supplemental bat roosting structures to aid in the conservation of tree roosting bats. The layered, rough surface created by the 3D printing process serves as a surface that bats can grip while roosting. Computer-aided design (CAD) models were generated based on natural roost structures, and a full-size bat house was successfully additively manufactured using a pellet-fed large-scale 3D printing system. The 3D printed hexagon exhibited a tensile strength of 22–23 MPa and a Young’s modulus of 3202–3218 MPa in the x-direction. It has been demonstrated that the 3D printed bat house can be installed on a tree in a stable fashion. This successful demonstration of a bat roost manufactured using a bioderived composite should promote its use in other fish and wildlife structures and broader industrial applications such as construction and automobiles.