Solar White Thermal Coating for Cryogenic Propulsion Systems

Jarred Wilhite; Jason Wendell

NASA NTRS · 20205006343

Solar White Thermal Coating for Cryogenic Propulsion Systems

Abstract

NASA is currently conducting research into the potential of storing cryogenic fluid in low Earth orbit (LEO). Having cryogenic propellant readily available for high-performance propulsion systems can be very beneficial for deep space missions in the near future. One of the key challenges to storing cryogenic fluid in LEO is minimizing boil-off. To address the challenge, NASA is evaluating new concepts in thermal insulation. One recent experimental study evaluated the feasibility of using Yttrium Oxide (Y2O3), formed into tiles or spray coating that can potentially be used as a thermal coating for cryogenic propellant storage applications in deep space. Due to its temperature and wavelength dependent optical properties, this “solar white” material can reflect a vast majority of the Sun’s radiative energy while having a very high infrared emissivity for rejecting heat to deep space. As a part of the material development and proof of concept testing, multiple tests have been run at KSC and GRC to demonstrate the performance of the material. At GRC, the tests were run using the Deep Space Solar Simulator (DS3) which contains a thermal vacuum chamber in which the solar white sample was exposed to a deep space environment (< 10 K, optically dense walls) while under full illumination via solar lamp. In order to improve the use of the test results and apply them to spacecraft, there is a need to be able to model the material properties within NASA’s standard thermal modeling tools. As such, it was set out to verify a thermal model of one of the experiments using Thermal Desktop with Sinda. The thermal model of the DS3 test setup includes the solar white sample along with a solar lamp simulator capable of outputting heat at varying wavelengths. The model was developed in order to validate the test results and also to help predict results that will be obtained in future tests. This paper will review the modeling methods and thermal analysis results for various test cases that were run within the DS3 facility.

Explore related subjects

Cryogenic Propulsion systems

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

Jarred Wilhite, Jason Wendell. Solar White Thermal Coating for Cryogenic Propulsion Systems. https://ntrs.nasa.gov/citations/20205006343

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

NASA NTRS2023

Fitting Leak Test Report: Ground-Based Cryogenic Leak Test of Fittings for Cryogenic Fluid Management

EXECUTIVE SUMMARY Mechanically connected joints used in cryogenic fluid lines as part of space flight elements need to survive launch vibrations and remain leak-free to minimize the loss of on-board commodity and hazardous gas accumulation. In 2020, a cryogenic test apparatus was developed which can evaluate the leak performance of pressurized threaded fluid fittings. The fittings were mounted in the TVAC and cooled to cryogenic test temperature and pressurized with helium while the leak rate was measured using a calibrated GHe leak detector. The test articles for the initial proof of concept testing were ¼ and 1 inch Swagelok VCR fittings with three different types of seal rings copper, nickel, and Ni. Each fitting configuration (size/seal material) was subjected to two consecutive cryogenic thermal cycles, followed by exposure to a launch vibration profile at ambient temperature, after which two additional TVAC cycle tests were performed. The testing reported here is a continuation of the 2020 tests with a statistically significant large number of samples and test runs. Three Swagelok VCR fitting sizes were tested ¼, ½ and 1 inch, and five (5) samples of each fitting size, each sample was tested with SST and Ni seal rings (Total of 30 unique test articles). Each test article was subjected to four (4) thermal cycles. Half of these cycles were performed before vibration testing and half were performed after vibration testing. The vibration testing was performed to evaluate the ability of the fittings to survive launch-type vibration profiles and remain leak-free. Leak checking of each fitting was completed at temperatures between 20K – 30K. The test procedure in Section 8.0 was designed to facilitate a qualification test program by allowing a higher test throughput rate coupled with repeatable test profiles. Results were very positive and show that out of the 30 samples they all passed with leak rates a factor of 2-3 lower than the established 10-6sccs GHe leak threshold. The result showed the Ni seals had lower leak rate, but the SST was more rugged. There were two deviations where damage to the Ni seal ring during assembly resulted in a leaky fitting, this is discussed in Section 10.7 Test Deviations. These fittings show great promise for space flight use and further testing is recommended to fully qualify the fittings per the ASTM F1387-19 and/or other relevant NASA specifications. The test equipment hardware and software capability developed for this testing is generic and not restricted to VCR fittings. It can be employed to evaluate/qualify the leak performance of other types of fittings and a wide range of other cryogenic fluid components such as valves, gages, connectors, etc.

Cryogenic↗

NASA NTRS2000

Verification Facility for Cryogenic Optics, Mechanisms, and Structures for the SIRTF Telescope

NASA's Space Infrared Telescope Facility (SIRTF) is a 1-meter class cryogenically-cooled space observatory.

Cryogenic↗

NASA NTRS1996

The SIRTF Telescope Test Facility: The First Year

The SIRTF Telescope Test Facility (STTF) consists of an optical dewar for testing mirrors of up to 1m diameter and f less than 6 at temperatures from 300K to 5K and a phase shift interferometer for optical characterization. The STTF was brought on line in early 1995.

Cryogenic↗