Sodium solid-state batteries (Na-SSB) have gained interest recently due to the abundance of Na over Li, but they still tend to fail due to dendrites under practical current densities and cycling capacities. To overcome this, Na-SSBs are frequently tested with impractically high applied pressure. In this work, a porous carbon interfacial layer is utilized in conjunction with Na-ß”-Al2O3 solid electrolytes to enable Na-cycling at milder cell pressures. This sodium/porous carbon layer enables improved solid-state Na cycling in symmetric cells, up to a current density of 10 mA cm-2 at 25 °C. Cycling up to 1 mAh cm-2 is challenging with low pressure, but 1 mAh cm-2 capacity can be reliably cycled at 1 mA cm-2 at an elevated temperature of 60 °C in symmetric cells. Finally, the evolution of the interface and sodium/carbon anode is evaluated with cryogenic ion-milling and cross-sectional imaging revealing that, depending on testing temperature, pressure, current density, and capacity, void formation, Na-extraction from porous carbon, delamination of the porous carbon matrix, or a combination of these occurs at the interface between Na-metal and BASE. Despite this, excellent dendrite resistance is achieved, and a full-cell design utilizing a Na-transition metal oxide cathode is still able to achieve an areal capacity of ~ 2.7 mAh cm-2 at 0.125 mA cm-2. This work demonstrates an alternative pathway toward a Na-metal anode for Na-SSBs without the requirement of excessive stack pressure.