FEA-Based Failure Analysis of Post-Buckled Composite Multi-Hat Stiffened Panel Under Static Compression

Abstract

The aerospace industry uses composite multi-hat stiffened panels for skins because of their high strength-to-weight and stiffness-to-weight ratios. However, laminated composites with initial flaws are susceptible to delamination under buckling loads. The goal is to ensure damage initiation occurs past the buckled state, only stable damage progression at loads below the ultimate compressive load, and debonding failure past the ultimate compressive load. This approach reduces weight and addresses a potential design review for future aircraft repairs. The need exists to better understand damage initiation and growth mechanisms in composite structures while assisting in the design, analysis, and sustainment methods. Teflon inserts simulate damage defects during manufacturing, while barely visible impact helps capture human error during manufacturing. This work shows the interaction between the skin-stringer and ply-ply separations at the post-buckled state for both defect events using Abaqus Virtual Crack Closure Technique (VCCT). The initial configuration for the Teflon case was to leave the Teflon region unbonded, and the initial impact damage region approximation came from the experimental data and was considered the initial configuration. When compared against the experimental data produced through the NASA Advanced Composites Project (ACP), the present model captured damage transition from skin-hat to ply1-ply2. The model validations were within ~5% of the experimental data.