NASA NTRS · 20240003137
The source did not provide an abstract. Follow the original record for more information.
Explore connections, maps & timelines
Eric Brizes. Materials Joining Automation in Low Earth Orbit. https://ntrs.nasa.gov/citations/20240003137
Cite the original work for its findings. Save a collection to share your selection of sources.
KEEP EXPLORING
In this welding test campaign, electron beam welding (EBW) and manual gas tungsten arc welding (GTAW) processes were utilized to join an additively manufactured aluminum alloy nozzle to a wrought aluminum flange. Both aluminum alloys were 6061, which in their conventional form are susceptible to solidification cracking issues. The AM nozzle utilized a novel high-performance modified version of 6061 which exhibits crack resistant properties during the AM process and during welding. When manually conducting GTAWs a filler wire with the same modified version of 6061 was utilized to weld different combinations of 6061 coupons (either modified or unmodified). Due to the grain refinement technology in the modified 6061, either as filler material or base material, there was complete elimination of weld solidification cracking. During EBW development a combination of wrought 6061 with a modified and additively manufactured 6061 was investigated. The EBWs developed exhibited no crack like defects. Each weld development program utilized non-destructive evaluation, metallography, and mechanical testing to determine the final weld acceptance. Mechanical testing involved hardness evaluation and tension testing on welded coupons. Both welding techniques were successfully developed and exhibited adequate properties for the final test articles and met all requirements of the development campaign. These welds were ultimately developed to be utilized on a set of all-aluminum liquid rocket nozzles to demonstrate additively manufactured aluminum alloys for propulsion applications. These aluminum nozzles were tested at NASA Marshall Space Flight Center’s hot fire test facility and subsequently underwent a test campaign involving a variety of chamber pressures and liquid propellant combinations. Following the hot fire test campaign each weldment was investigated for post operation performance and any defects that may have evolved during testing.
In this study the NASA MSFC welding and manufacturing team investigated a new-age aluminum filler wire designed for welding and additive manufacturing (AM) of high strength aluminum alloys. High strength aluminum alloys are known to exhibit hot cracking and hot tearing issues during fusion welding operations. The goal of this investigation was to determine whether this new-age family of alloys can suppress the hot cracking and hot tearing issues exhibited during welding of high strength aluminum alloys and to do an initial characterization of the mechanical performance of welds created using these filler wires. This study focuses on fusion welding of aluminum alloy 6061 and compares the weldability characteristics of five aluminum filler metals and two forms of 6061 base material. The MSFC team utilized manual gas tungsten arc welding (GTAW) to conduct all welding operations and carried out metallographic analysis accompanied with mechanical testing to evaluate the performance of the welds created during this study. During the study it was observed that the new-age filler wires facilitated grain refinement in the weld fusion zone and were capable of creating crack free welds in aluminum alloy 6061 while exhibiting properties that met or exceeded conventional off the shelf aluminum filler metals.
Explore the source record for details and available documents.