David E Glass. Ceramic Matrix Composites: The Next Material Revolution?. https://ntrs.nasa.gov/citations/20240011832
Cite the original work for its findings. Save a collection to share your selection of sources.
KEEP EXPLORING
High-cycle fatigue (HCF) behavior of a melt-infiltrated, prepreg SiC/SiC composite was investigated using specimens without and with simulated cooling holes at 816 and 1,316 °C. The ceramic-matrix composite (CMC) material used for this study was fabricated by GE Aviation and had a ply configuration of [0/90/0] 3 . HCF tests were conducted with an R-ratio of 0.6 and a cyclic frequency of 30 Hz. Maximum tensile gross-section stresses used in the HCF tests ranged from 152 to 359 MPa. Runout in HCF was defined as 30 million cycles (278 h) at both temperatures. Monotonic tensile tests were conducted at room temperature (RT) on as-received CMC specimens and on HCF runout specimens without and with holes to determine residual tensile strengths. Digital image correlation (DIC) and acoustic emission (AE) techniques were used to monitor progression of damage in RT tensile tests on specimens without and with holes. Fractography was performed on a limited number of specimens without and with holes to determine morphology of fracture surfaces. Representative RT stress-strain behavior, elevated temperature HCF behavior at the two temperatures, and RT residual tensile strengths of HCF runout specimens are documented in this report. Select examples of DIC and AE data from RT tensile tests on specimens without and with holes and typical features observed on fracture surfaces of specimens tested under tensile and HCF conditions are also discussed.
Ceramic matrix composites (CMCs) such as SiCSiC are currently being designed and implemented in high temperature sections of aerospace turbine engines. Such components will be subject to through-thickness thermal gradients, which may affect the durability. In this study, SiCSiC CMCs with a hybrid chemical vapor infiltrated (CVI) and polymer infiltration and pyrolysis (PIP) matrix were loaded in tension while one surface was heated with a laser and the opposite surface was cooled. The samples were each coated with an environmental barrier coating (EBC), which was produced by electron beam physical deposition (EBPVD). Results for CMCs tested with and without the EBC be discussed.
Ceramic matrix composites (CMCs) such as SiC/SiC are currently being designed and implemented in high temperature sections of aerospace turbine engines. Such components will be subject to through-thickness thermal gradients, which may affect the durability. In this study, SiC/SiC CMCs with a hybrid chemical vapor infiltrated (CVI) and polymer infiltration and pyrolysis (PIP) matrix were loaded in tension while one surface was heated with a laser and the opposite surface was cooled. Issues associated with laser testing will be discussed, along with initial results for coated and uncoated samples.