NASA NTRS · 20250000115

Environmental Barrier Coating Surface Temperature Mapping Using a Compatible Er-Doped Sc 2 SiO 5 Temperature-Sensing Layer

Jeffrey I Eldridge·Kang N Lee·John A Setlock
View original source ↗Export metadata ↓

Abstract

Accurate surface temperature-mapping capabilities in the 1300 to 1500 °C range are needed for SiC/SiC ceramic matrix composites protected by environmental barrier coatings (EBCs) under testing in turbine engine environment facilities. The strong background thermal radiation at these higher temperatures is a challenging issue. Er-doped Y 2 SiO 5 was previously shown to be capable of achieving luminescence lifetime-based temperature mapping up to 1560 °C as a standalone material. However, compatibility issues between an Er-doped Y 2 SiO 5 surface temperature sensing layer and an underlying Sc 2 Si 2 O 7 -based EBC topcoat limited temperature mapping of the EBC surface to a maximum of 1380 °C. Therefore, an Er-doped Sc 2 SiO 5 temperature sensing layer has been subsequently developed with better compatibility with the Sc2Si2O7-based EBC topcoat. Localized spot temperature measurements as well as luminescence lifetime imaging-based temperature mapping were demonstrated up to 1535 °C from a 15 µm thick Er-doped Sc 2 SiO 5 layer at the surface of a Sc2Si2O7-based EBC topcoat, a significant improvement over the Er-doped Y2SiO5 layer 1380 °C temperature sensing limit. No degradation of the Er-doped Sc 2 SiO 5 temperature sensing surface layer was observed.

Explore related subjects

temperature measurementluminescenceenvironmental barrier coating

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Jeffrey I Eldridge, Kang N Lee, John A Setlock. Environmental Barrier Coating Surface Temperature Mapping Using a Compatible Er-Doped Sc 2 SiO 5 Temperature-Sensing Layer. https://ntrs.nasa.gov/citations/20250000115

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

NASA NTRSDate not supplied

Temperature Sensing to Above 1500 °C Using Y 2 SiO 5 :Er Phosphor Thermometry

A transition from metallic to ceramic turbine components that can operate at higher turbine engine temperatures will push component surface temperatures from below 1200 °C into a 1300 to 1500 °C temperature range that is much more challenging for phosphor thermometry measurements. To address this challenge, Y 2 SiO 5 :Er was selected for its high temperature sensing performance by both luminescence lifetime and luminescence intensity ratio (LIR) methods as well as its thermochemical compatibility with the current generation of rare earth silicate environmental barrier coatings (EBCs) that are required to protect SiC/SiC ceramic composite components. Lifetime measurements that monitor the Er3+ 4S3/2→4I15/2 emission decay at 542 nm exhibited a slow decrease in decay time with temperature up to 1300° C, above which the decay decreased steeply to provide good temperature sensitivity in the 1300 to 1500 °C range (Fig. 1). LIR images were obtained where each pixel represented the ratio I488/I561 (I488 and I561 are the detected 488 nm 4F7/2→4I15/2 and the 561 nm 4S3/2→4I15/2 emission band intensities, respectively). Good temperature sensitivity (Fig. 2) and signal-to-background ratios were observed to above 1500 °C. Contrary to conventional guidance on selecting phosphors for high temperature sensing, the detected emission band intensities and decay times exhibited remarkably slow decreases with temperature up into the 1300 to 1500 °C range despite high phonon energies (>900 cm-1) that allow the energy gap between the 4S3/2 emitting reservoir level and the 4F9/2 level below it to be bridged by as few as three phonons. The benefits of utilizing a thermographic phosphor at very high temperatures that exhibits strong nonradiative multiphonon relaxation even at room temperature is explained by a competition between spontaneous and stimulated multiphonon emission, and the more temperature-sensitive decay time above 1300 °C is explained by a transition from high to low effective phonon energies.

temperature measurement↗
NASA NTRSDate not supplied

Development of Luminescence Lifetime-Based Surface Temperature Mapping for Environmental Barrier Coatings

Luminescence lifetime-based temperature mapping for thermal barrier coatings (TBCs) has been previously demonstrated up to temperatures approaching 1200 °C. Advantages of this method include insensitivities to reflected radiation and emissivity uncertainties. Because of a push towards greater efficiency turbine engine operation using higher turbine inlet temperatures, there is an ongoing movement from TBC-coated superalloy turbine engine components to SiC/SiC ceramic matrix composite components protected by environmental barrier coatings (EBCs). The useful application of luminescence lifetime-based temperature mapping to EBCs requires a significant increase in high temperature capability from below 1200 °C up into the 1300 to 1500 °C temperature range where the much higher background thermal radiation is a challenging issue. In addition, the luminescing sensing layer must exhibit thermochemical compatibility with the EBC. To meet these requirements, Er-doped Y 2 SiO 5 was selected as the luminescing sensor layer material both for its enhanced temperature sensitivity above 1300 °C and its compatibility with rare-earth disilicate EBC topcoats. Both localized spot temperature measurements as well as luminescence lifetime imaging-based temperature mapping were demonstrated up to 1560 °C for Er-doped Y 2 SiO 5 disks. In addition, temperature mapping capability was demonstrated from a 15 µm thick Er-doped Y 2 SiO 5 layer at the surface of a Sc 2 Si 2 O 7 based EBC topcoat. Both localized spot and temperature mapping by luminescence lifetime imaging were demonstrated up to 1380 °C (upper temperature limit of this slurry-based layered EBC) with excellent suppression of background thermal radiation and no degradation of the Er-doped Y 2 SiO 5 temperature sensing surface layer. The source of the novel enhanced temperature sensitivity above 1300 °C will be discussed as well as a path towards compatibility between sensing layer and EBC topcoat to higher temperatures.

temperature measurement↗