Polymer Composite Material Screening for a Cryotank Application

Composite cryotanks will play a key role in enabling the next generation of efficient aircraft. Carbon fiber reinforced polymer (CFRP) composites have the benefits of reduced weight and potentially higher structural strength compared to traditional metallic fuel tanks. A material screening study was conducted to inform material selection for liquid hydrogen (LH2) fuel storage. Three composite materials were considered because of their aerospace grade toughness, strength, and existing data to compare against. These materials were a thermoplastic low-melt polyaryletherketone (LM-PAEK)/carbon fiber (CF), thermoset/CF, and hybrid thermoset/thermoplastic polyurethane (TPU) veil/CF composite. Mechanical screening tests included tension, compression, in-plane shear (IPS), and tensile-tensile fatigue (TTF). Each material was tested at both a baseline (no liquid nitrogen/LN2 cycling) and 100 LN2-cycled conditions to determine the knockdown factor, if any, of each material when exposed to environmental loading effects in a cryotank. Results show minimal effects of the LN2-cycling compared against baseline values. The three materials behaved similarly in tension; however, the thermoplastic/CF had the highest IPS toughness. The hybrid thermoset/TPU/CF composite had the lowest IPS strength, compressive strength, and toughness. LN2-cycling had minimal effects on tensile-tensile fatigue performance of the thermoplastic/CF material. Mechanical data was captured to guide material down selection for future commercially viable hydrogen aircraft design. In its current state, there does not exist a consolidated, publicly available database for CFRP composite material performance data at cryogenic temperatures. The next step in this work is to test the thermoplastic and thermoset CFRP composites, as well as the neat resins, at LH2 relevant temperature (20 K) to capture this crucial material property data. These results are essential to inform cryotank design and modeling efforts. The process to start this next round of testing has begun. Planned mechanical tests include toughness (single-edge notched beam), tension (unidirectional and quasi-isotropic), thermal expansion, and thermal conductivity. Some tests will also be conducted at an intermediate temperature of 111 K relevant to liquid natural gas (LNG), another attractive fuel choice. The ultimate goal is to manufacture a sub-scale cryotank part that can pass relevant burst, fatigue, permeation, and thermal cycling tests. This work is a part of NASA’s Commercially viable Hydrogen Aircraft for Robust Growth in Efficiency (CHARGE) Project under the larger NASA Subsonic Vehicle Technologies and Tools (SVTT) Project.

composites↗

NASA NTRS2026

Thermoplastic Matrix Composite Design for Cryotanks Using Multiscale Modeling and Bayesian Optimization

Designing lightweight, robust cryogenic storage tanks is critical for future launch vehicles, in-space propellant storage, and hydrogen powered aircraft. This work presents a multiscale modeling and Bayesian optimization framework for the design of thermoplastic matrix composite cryotanks. Molecular dynamics simulations are first used to determine temperature-dependent constituent properties for candidate thermoplastic matrices, which are homogenized to the lamina scale using NASA’s Multiscale Analysis Tool (NASMAT). These lamina properties, in combination with laminate family generation rules, are evaluated in HyperX structural optimization software to identify stacking sequences that meet all cryogenic load requirements. A Bayesian optimization framework is applied, with HyperX in the loop (via the HyperX API) to efficiently search across material and laminate design variables, yielding an optimized cryotank configuration with significant reductions in design cycle time compared to exhaustive search approaches.

thermoplastics↗

DOE OSTI2026

Evaluating Fracture Behavior of Bioinspired Alumina-YSZ Composites through Static and Dynamic Mechanical Testing

Ceramic materials are known for their high hardness and strength but are limited by low toughness and sudden failure. Inspired by the microstructure of dental enamel, which features undulating rods that promote crack deflection and energy absorption, architected specimens were designed and manufactured. A bespoke ball-on-ring (BoR) testing apparatus measured the static biaxial rupture strength of these bioinspired materials. Additionally, impact testing with spherical steel projectiles assessed their behavior under dynamic conditions. Monolithic alumina specimens were compared to architected alumina reinforced with yttria-stabilized zirconia (YSZ) rods produced via direct ink write 3D printing. BoR tests revealed that monolithic alumina had a Weibull modulus of 10.53 and a characteristic strength of 372.3 MPa, while the composite specimens showed a Weibull modulus of 5.46 and a characteristic strength of 213.3 MPa. Although the composite failed at lower stresses and projectile velocities, it exhibited notable crack deflection and fracture resistance, with cracks being effectively interrupted by the rod inclusions. The composite specimens also resulted in fewer and larger fragments upon impact. Finite element simulations confirmed the effectiveness of the rod structures in enhancing fracture resistance.

Bioinspired materials↗