Comparison Testing and Analysis of Braided Cords Constructed from Varying Kevlar Fiber Types

Abstract

Material advancements move quickly, resulting in material obsolescence issues that require parachute engineers to understand how the material properties change with a material upgrade and if there are expected impacts to overall performance of the parachute. The objective of this test was to measure the elongation of different Kevlar types at both the cord-level and at the yarn-level to determine if a change in Kevlar type impacted parachute performance. An Instron machine with a pin-to-pin connection was used to measure load and displacement time histories for various Kevlar cord and yarn samples in a cyclic load profile. Twenty-four cord samples and twenty-four yarn samples were tested; each sample was cycled five times to the relevant maximum load (either to breaking strength or to the 30% peak load expected in flight). In addition to the Instron measurements, a photogrammetric technique was also implemented to measure elongation of the samples using button targets. Modulus test data shows approximately a 10% difference in elongation between Kevlar 29AP and Kevlar 129, and another 10% difference in elongation between Kevlar 29 and Kevlar 29AP. Although this is a measurable change in modulus, the effect on parachute performance is likely small, particularly for non-primary structure elements of relatively small length. This test campaign provides an example of the type of testing and analysis that parachute engineers could do to understand how material upgrades affect performance of their systems.