In-Situ Scanning Electron Microscope Experiments for Microscale Mechanical Testing and Validated Modeling of Fiber Reinforced Thermoplastics

Abstract

A novel, in-situ, scanning electron microscope (SEM) mechanical testing capability for materials at the microscale which provides experimental validation to a machine learning (ML) toolset for full-field validation of physics-based micromechanics models is being developed by researchers at NASA Glenn Research Center. These are enabling technologies for the integration of multiscale digital twins for materials into system level models which will result in the improved performance, material discovery, reduced production cost and time, rapid characterization, and prognostic structural health monitoring (SHM) for materials and structures for extreme environments in support of NASA space exploration missions. In order to bridge the material structure-to-system gap for digital twins, physics-based models must be experimentally validated at multiple length scales. Seminal microscale experiments, conducted at the Air Force Research Laboratory (AFRL), were limited to transverse compression of single-layer, unidirectional thermoset polymer matrix composite (PMC) micropillar specimens [1]. The early phases of the current project followed those initial results and setup to reproduce the compression testing of PMC material on the custom-built piezoelectric actuated micromechanical testing rig built by MicroTesting Solutions LLC. In this work, samples of thermoplastic PMC material were first machined into 3 mm cubes, and then further machining and final milling was done using a Focused Ion Beam (FIB). The initial experiment was done on a pillar roughly 20 µm x 20 µm x 40 µm tall. Additional pillars were milled with final sizes ranging from 20 µm x 20 µm x 40 µm tall to 40 µm x 40 µm x 65 µm tall. A speckle pattern for in-situ full-field measurements using Digital Image Correlation (DIC) was applied with platinum, which was coated on the surface, and then the FIB was used to mill away some of the coating to produce an irregular pattern of Pt on the pillar surface. The samples were loaded into the custom testing rig and placed into the SEM and loaded under compression until failure. Images were collected in the SEM during testing. Post-processing of the images was conducted using DIC to obtain full-field displacement and strain measurements elucidating the role of the matrix as well as fiber-fiber interaction at the microscale within the composite subjected to compression loading well into the non-linear regime of the material. Moreover, the evolution of fiber-matrix debonding and matrix cracking is observed in-situ at the microscale. This data, along with images segmented with a newly developed ML toolset [2], was used to create and validate physics-based micromechanics models. An image of the failed micropillar is shown in Figure 1. The techniques developed in the initial compression experiment was tailored to the validation needs of the models and expanded to include different sized samples as well as possibly tension and fatigue.