Polymer Composite Material Testing for a Cryotank Application

Abstract

Composite cryotanks will play a key role in enabling the next generation of efficient aircraft. Carbon fiber reinforced polymer (CFRP) composites have the benefits of reduced weight and potentially higher structural strength compared to traditional metallic fuel tanks. A material screening study was conducted to inform material selection for liquid hydrogen (LH2) fuel storage. Three composite materials were considered because of their aerospace grade toughness, strength, and existing data to compare against. These materials were a thermoplastic low-melt polyaryletherketone (LM-PAEK)/carbon fiber (CF), thermoset/CF, and hybrid thermoset/thermoplastic polyurethane (TPU) veil/CF composite. Mechanical screening tests included tension, compression, in-plane shear (IPS), and tensile-tensile fatigue (TTF). Each material was tested at both a baseline (no liquid nitrogen/LN2 cycling) and 100 LN2-cycled conditions to determine the knockdown factor, if any, of each material when exposed to environmental loading effects in a cryotank. Results show minimal effects of the LN2-cycling compared against baseline values. The three materials behaved similarly in tension; however, the thermoplastic/CF had the highest IPS toughness. The hybrid thermoset/TPU/CF composite had the lowest IPS strength, compressive strength, and toughness. LN2-cycling had minimal effects on tensile-tensile fatigue performance of the thermoplastic/CF material. Mechanical data was captured to guide material down selection for future commercially viable hydrogen aircraft design. In its current state, there does not exist a consolidated, publicly available database for CFRP composite material performance data at cryogenic temperatures. The next step in this work is to test the thermoplastic and thermoset CFRP composites, as well as the neat resins, at LH2 relevant temperature (20 K) to capture this crucial material property data. These results are essential to inform cryotank design and modeling efforts. The process to start this next round of testing has begun. Planned mechanical tests include toughness (single-edge notched beam), tension (unidirectional and quasi-isotropic), thermal expansion, and thermal conductivity. Some tests will also be conducted at an intermediate temperature of 111 K relevant to liquid natural gas (LNG), another attractive fuel choice. The ultimate goal is to manufacture a sub-scale cryotank part that can pass relevant burst, fatigue, permeation, and thermal cycling tests. This work is a part of NASA’s Commercially viable Hydrogen Aircraft for Robust Growth in Efficiency (CHARGE) Project under the larger NASA Subsonic Vehicle Technologies and Tools (SVTT) Project.