Exposure of Highly Reflective Far-Ultraviolet Coatings to LEO Environment for TRL Advancement for the Habitable Worlds Observatory

Abstract

Over the past several years, our team at the NASA Goddard Space Flight Center (GSFC), in collaboration with the Jet Propulsion Laboratory (JPL) and the Naval Research Laboratory (NRL), have developed several new protected Al coating technologies with improved Far-Ultraviolet (FUV) reflectance performance and more robust environmental stability. These include Al protected with lithium-based fluoride (LiF) coatings such as hot deposited LiF (eLiF), XeF 2 -passivated LiF coatings (XeLiF), Li 3 AlF 6 overcoats, AlF 3 (plasma passivated), and XeF 2 passivated MgF 2 coatings (XeMgF 2 ). However, despite these developments, relatively little experimental information exists regarding the long-term stability of these coatings after simultaneous exposure to the Low Earth Orbit (LEO) environment. To evaluate their environmental durability and advance their Technology Readiness Level (TRL), representative samples of these coating technologies, Al+XeLiF, Al+eLiF, Al+Li 3 AlF 6 , Al+AlF 3 , Al+XeMgF 2 , and bare Al as reference samples, were flown onboard the International Space Station (ISS) as part of the Materials International Space Station Experiment 20 (MISSE-20). The MISSE platform is operated by Aegis Aerospace for relatively long-duration (e.g. 6 months) external exposure experiments in a space environment. The coatings were deposited on ULE and Zerodur substrates, and witness samples deposited on the same coatings runs, but on glass slides were left on Earth as control. A subset of the flight samples were fitted with MgF 2 windows to reduce direct exposure to atomic oxygen (AO) and charged particles, and still let through UV and other types of radiation on these samples. After approximately 6 months of exposure in the forward-facing (RAM) direction, the samples were returned to Earth and characterized by performing FUV/NUV/VIS/NIR reflectance measurements to quantify degradation, spectroscopic ellipsometry to evaluate coating thickness and optical constants, atomic force microscopy (AFM) to quantify surface roughness evolution during the flight in the ISS. The MgF 2 protective windows were also analyzed through FUV transmission measurements. Comparison with the witness samples left on the ground and with the flown bare Al samples (with just the naturally occurring Al 2 O 3 layer) provided a quantitative assessment of coating thickness variations, optical performance degradation, and morphological changes induced by prolonged exposure to the LEO environment.