NASA NTRS · 20260007852
The source did not provide an abstract. Follow the original record for more information.
Michael Chauby. 2026-08-26. Fire Retardant Aerogels Made From a Polybenzimidazole Backbone. https://ntrs.nasa.gov/citations/20260007852
Cite the original work for its findings. Save a collection to share your selection of sources.
KEEP EXPLORING
Biogenic thermal insulation materials are in high demand because of its carbon-sequestration nature. However, high flammability, moisture condensation, and relatively high thermal conductivity of biogenic material are major concerns for sustainable building applications. In this study, we report the fire-retardant cellulose xerogel insulation nanocomposites derived from hemp fiber recycling and silica xerogel, in which the boric acid treatment improves its fire retardancy. The as-prepared materials show a low thermal conductivity of 31.3 mW/m K, high flexural modulus of 665 MPa, hydrophobicity with the water contact angle of 115°, and fire retardancy with 30% weight loss over a period of burning time 10 min. Overall, this work provides an effective method for the synthesis of fire-retardant biogenic thermal insulation materials and shows a promising way for next-generation bio-based insulation materials.
Advanced aerospace vehicular concepts require advances in many existing technologies, including space power and energy storage systems. Batteries represent one of the major areas in need of improvement, both in terms of energy density and safety, with growing concerns over the fire safety of commercial lithium-ion batteries. This has prompted efforts to develop nonflammable battery components, namely the electrolyte and separator. Existing commercial lithium-ion batteries utilize polyolefin microporous membranes as separators with an electrolyte consisting of a lithium salt dissolved in a mixture of cyclic carbonate solvents. This separator/electrolyte combination has ionic conductivities in the range of 10 −2 to 10 −3 S/cm. However, the cyclic carbonate solvents are inherently flammable. Room-temperature ionic liquids (RTILs) appear to be a safer alternative. They offer good ionic conductivities and are inherently nonvolatile and nonflammable, giving them a safety advantage. However, many promising RTILs for battery electrolytes are not compatible with commercial polyolefin separator materials. Alternative separator materials, such as polyimides, are non-flammable and are capable of accepting RTILs into their structure. Polyimide gels, with a composition of 4,4′-oxydianiline, 3,3′,4,4′-tetracarboxylic dianhydride and cross-linked with Desmodur N3300A, possess an open-porous, fibrillar network architecture which offers a high degree of porosity (typically greater than 85% porosity) for lithium-ion transport and conduction, as well as good mechanical properties. Furthermore, these polyimide gels are compatible with selected imidazolium-based RTILs. Nonflammable separator/electrolyte systems with room-temperature conductivities in the range of 10 −3 S/cm have been evaluated. It has been demonstrated that 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide was the most promising among six RTILs screened, in terms of both ionic conductivity and constant current cycling.
The Aerogel Lecture Series unveils the extraordinary potential of aerogels—a class of highly porous solid materials derived from a gel in which the liquid is replaced by gas while maintaining the self-assembled three-dimensional structure. This video presentation features Dr. Sadhan Jana from University of Akron.