NASA NTRS · 20260007857
The source did not provide an abstract. Follow the original record for more information.
Sarah Stewart, Sam Keller, Sydney Taylor, Ognjen Ilic. Variable Emittance Coating Systems Thermal Modeling for a 3U CubeSat. https://ntrs.nasa.gov/citations/20260007857
Cite the original work for its findings. Save a collection to share your selection of sources.
KEEP EXPLORING
Discs coated with spray-on solar white and two similar thermal control coatings were flown in low earth orbit for roughly five hours. While in orbit, the coated discs were exposed to direct sunlight and to deep space for short intervals. Measurements of disc temperatures showed that the spray-on solar white coating had the lowest absorption of sunlight. Numerical modeling was used to infer that spray-on solar white had a solar absorptance between 0.02 and 0.04 and a thermal emittance between 0.93 and 0.99, both of which are consistent with terrestrial laboratory measurements.
Passive thermal control is necessary as space exploration becomes increasingly widespread. Materials with superior optical properties (high solar reflectance and infrared emittance) are critical for passive thermal control because they can reject most of the incident solar radiation and promote thermal emission from cryogenic propellant storage tanks, enabling the extraterrestrial storage of cryogens. We have demonstrated in previous studies that electrospun nanofibers exhibit exceptional optical properties, offering significant benefits for passive radiative cooling in space. Particularly, electrospun polyvinylidene fluoride-co-hexafluoropropylene PVDF-HFP nanofibers demonstrate exceptionally high solar reflectance (>99%) and strong thermal emittance (measured at ~300 K). However, they exhibit nanostructural changes in the presence of atomic oxygen, which is prevalent in Low Earth Orbit. This study focuses on creating a unique blend of polymeric (PVDF-HFP) and ceramic-based (silica) nanofibers by leveraging the chemical stability and atomic oxygen resistance of silica, using the dual electrospinning manufacturing method. This approach aims to preserve the structural properties of the polymeric counterpart without compromising its optical performance, thereby providing an innovative method for manufacturing environmentally resilient passive thermal control nanofibers with desirable optical and thermal control functionalities for extraterrestrial storage of cryogenic propellants.
Cryogenic propellant passive thermal management techniques in space are essential complements to active thermal management methods, helping reduce absolute dependence on the latter. Particularly, materials with superior optical properties (high solar reflectance and infrared emittance) would be beneficial for passive thermal control to reject most of the incident solar radiation and enhance thermal emission from the storage tank, leading to self-cooling. We developed a nanofibrous, porous passive thermal control material by electrospinning polyvinylidene fluoride-co-hexafluoropropylene (PVDF-HFP) co-polymer onto an aluminum foil substrate. The material exhibits a very high solar reflectance (>99%) and infrared emittance (~86%) when characterized in the ultraviolet-visible-near infrared and mid-infrared wavelengths. This study focuses on the adhesion of the nanofibrous PVDF-HFP to the substrate. We incorporated in-lab fabricated and commercial adhesives, under normal room conditions, between the nanofibers and the aluminum foil substrate to improve their adhesion. Some samples were also exposed to space-like conditions – vacuum and thermal cycling, to investigate their effects on the strengths of adhesives. Subsequently, adhesion peel tests were conducted on all the samples to assess the peel strengths of the bonds. Peel test strengths after space environment conditioning of the adhesives were generally higher than those observed in the pristine, unaged samples. The results are discussed in this study.