Materials Data on Ba4Ti12O27 by Materials Project

Abstract

Ba4Ti12O27 crystallizes in the monoclinic C2/m space group. The structure is three-dimensional. there are three inequivalent Ba2+ sites. In the first Ba2+ site, Ba2+ is bonded in a 12-coordinate geometry to twelve O2- atoms. There are a spread of Ba–O bond distances ranging from 2.81–3.21 Å. In the second Ba2+ site, Ba2+ is bonded in a 12-coordinate geometry to eleven O2- atoms. There are a spread of Ba–O bond distances ranging from 2.78–2.95 Å. In the third Ba2+ site, Ba2+ is bonded in a 11-coordinate geometry to eleven O2- atoms. There are a spread of Ba–O bond distances ranging from 2.73–3.20 Å. There are ten inequivalent Ti+3.83+ sites. In the first Ti+3.83+ site, Ti+3.83+ is bonded to six O2- atoms to form TiO6 octahedra that share corners with four equivalent TiO6 octahedra and corners with two equivalent TiO5 square pyramids. The corner-sharing octahedral tilt angles are 6°. There are two shorter (2.03 Å) and four longer (2.05 Å) Ti–O bond lengths. In the second Ti+3.83+ site, Ti+3.83+ is bonded to six O2- atoms to form a mixture of edge and corner-sharing TiO6 octahedra. The corner-sharing octahedral tilt angles are 16°. There is two shorter (1.97 Å) and four longer (2.00 Å) Ti–O bond length. In the third Ti+3.83+ site, Ti+3.83+ is bonded to six O2- atoms to form TiO6 octahedra that share corners with two equivalent TiO6 octahedra, corners with two equivalent TiO5 square pyramids, and edges with four TiO6 octahedra. The corner-sharing octahedral tilt angles are 50°. There are four shorter (1.99 Å) and two longer (2.01 Å) Ti–O bond lengths. In the fourth Ti+3.83+ site, Ti+3.83+ is bonded to six O2- atoms to form TiO6 octahedra that share corners with two equivalent TiO6 octahedra, corners with two equivalent TiO5 square pyramids, and edges with three TiO6 octahedra. The corner-sharing octahedral tilt angles are 12°. There are a spread of Ti–O bond distances ranging from 1.92–2.08 Å. In the fifth Ti+3.83+ site, Ti+3.83+ is bonded to six O2- atoms to form a mixture of distorted edge and corner-sharing TiO6 octahedra. The corner-sharing octahedra tilt angles range from 16–52°. There are a spread of Ti–O bond distances ranging from 1.86–2.17 Å. In the sixth Ti+3.83+ site, Ti+3.83+ is bonded to six O2- atoms to form TiO6 octahedra that share corners with two equivalent TiO6 octahedra, edges with four TiO6 octahedra, and an edgeedge with one TiO5 square pyramid. The corner-sharing octahedral tilt angles are 55°. There are a spread of Ti–O bond distances ranging from 1.94–2.09 Å. In the seventh Ti+3.83+ site, Ti+3.83+ is bonded to five O2- atoms to form a mixture of distorted edge and corner-sharing TiO5 square pyramids. The corner-sharing octahedra tilt angles range from 3–30°. There are a spread of Ti–O bond distances ranging from 1.82–2.04 Å. In the eighth Ti+3.83+ site, Ti+3.83+ is bonded to six O2- atoms to form a mixture of edge and corner-sharing TiO6 octahedra. The corner-sharing octahedra tilt angles range from 6–47°. There are a spread of Ti–O bond distances ranging from 1.89–2.16 Å. In the ninth Ti+3.83+ site, Ti+3.83+ is bonded to six O2- atoms to form a mixture of edge and corner-sharing TiO6 octahedra. The corner-sharing octahedra tilt angles range from 50–55°. There are a spread of Ti–O bond distances ranging from 1.89–2.15 Å. In the tenth Ti+3.83+ site, Ti+3.83+ is bonded to six O2- atoms to form a mixture of distorted edge and corner-sharing TiO6 octahedra. The corner-sharing octahedra tilt angles range from 40–53°. There are a spread of Ti–O bond distances ranging from 1.84–2.18 Å. There are sixteen inequivalent O2- sites. In the first O2- site, O2- is bonded in a distorted see-saw-like geometry to four Ti+3.83+ atoms. In the second O2- site, O2- is bonded in a distorted trigonal planar geometry to three Ti+3.83+ atoms. In the third O2- site, O2- is bonded in a 4-coordinate geometry to one Ba2+ and three Ti+3.83+ atoms. In the fourth O2- site, O2- is bonded in a 3-coordinate geometry to one Ba2+ and three Ti+3.83+ atoms. In the fifth O2- site, O2- is bonded in a distorted linear geometry to three Ba2+ and two Ti+3.83+ atoms. In the sixth O2- site, O2- is bonded in a distorted linear geometry to four Ba2+ and two Ti+3.83+ atoms. In the seventh O2- site, O2- is bonded in a 3-coordinate geometry to two Ba2+ and three Ti+3.83+ atoms. In the eighth O2- site, O2- is bonded in a distorted water-like geometry to two equivalent Ba2+ and two Ti+3.83+ atoms. In the ninth O2- site, O2- is bonded in a 4-coordinate geometry to one Ba2+ and three Ti+3.83+ atoms. In the tenth O2- site, O2- is bonded in a 2-coordinate geometry to two Ba2+ and two Ti+3.83+ atoms. In the eleventh O2- site, O2- is bonded in a distorted trigonal planar geometry to three Ti+3.83+ atoms. In the twelfth O2- site, O2- is bonded in a distorted linear geometry to three Ba2+ and two Ti+3.83+ atoms. In the thirteenth O2- site, O2- is bonded in a 4-coordinate geometry to one Ba2+ and three Ti+3.83+ atoms. In the fourteenth O2- site, O2- is bonded in a 2-coordinate geometry to two Ba2+ and two Ti+3.83+ atoms. In the fifteenth O2- site, O2- is bonded in a distorted T-shaped geometry to two Ba2+ and three Ti+3.83+ atoms. In the sixteenth O2- site, O2- is bonded in a 4-coordinate geometry to one Ba2+ and three Ti+3.83+ atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on Ba4Ti12O27 by Materials Project. https://doi.org/10.17188/1191361

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗