Materials Data on CoN3 by Materials Project

View original source ↗Read source document ↗Export metadata ↓

Abstract

CoN3 is Skutterudite structured and crystallizes in the cubic Im-3 space group. The structure is three-dimensional. Co3+ is bonded to six equivalent N1- atoms to form CoN6 octahedra that share corners with six equivalent CoN6 octahedra and corners with twelve equivalent NCo2N2 tetrahedra. The corner-sharing octahedral tilt angles are 72°. All Co–N bond lengths are 1.94 Å. N1- is bonded to two equivalent Co3+ and two equivalent N1- atoms to form distorted NCo2N2 tetrahedra that share corners with four equivalent CoN6 octahedra, corners with ten equivalent NCo2N2 tetrahedra, and an edgeedge with one NCo2N2 tetrahedra. The corner-sharing octahedra tilt angles range from 64–66°. There is one shorter (1.45 Å) and one longer (1.56 Å) N–N bond length.

Explore related subjects

36 MATERIALS SCIENCECo-NCoN3crystal structure

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-22. Materials Data on CoN3 by Materials Project. https://doi.org/10.17188/1198956

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗