Materials Data on Na3SiSe4 by Materials Project

Abstract

Na3SiSe4 crystallizes in the monoclinic P2_1/c space group. The structure is three-dimensional. there are six inequivalent Na1+ sites. In the first Na1+ site, Na1+ is bonded to six Se+1.75- atoms to form distorted NaSe6 octahedra that share a cornercorner with one NaSe6 octahedra, corners with four SiSe4 tetrahedra, corners with two equivalent NaSe5 trigonal bipyramids, edges with four NaSe6 octahedra, an edgeedge with one SiSe4 tetrahedra, and an edgeedge with one NaSe5 trigonal bipyramid. The corner-sharing octahedral tilt angles are 12°. There are a spread of Na–Se bond distances ranging from 2.86–3.47 Å. In the second Na1+ site, Na1+ is bonded to six Se+1.75- atoms to form distorted NaSe6 octahedra that share corners with two equivalent NaSe6 octahedra, corners with four SiSe4 tetrahedra, corners with two equivalent NaSe5 trigonal bipyramids, edges with three NaSe6 octahedra, an edgeedge with one SiSe4 tetrahedra, and an edgeedge with one NaSe5 trigonal bipyramid. The corner-sharing octahedra tilt angles range from 13–39°. There are a spread of Na–Se bond distances ranging from 2.92–3.63 Å. In the third Na1+ site, Na1+ is bonded in a 5-coordinate geometry to five Se+1.75- atoms. There are a spread of Na–Se bond distances ranging from 2.92–3.34 Å. In the fourth Na1+ site, Na1+ is bonded in a 6-coordinate geometry to six Se+1.75- atoms. There are a spread of Na–Se bond distances ranging from 2.93–3.36 Å. In the fifth Na1+ site, Na1+ is bonded to five Se+1.75- atoms to form NaSe5 trigonal bipyramids that share corners with four NaSe6 octahedra, corners with three SiSe4 tetrahedra, edges with five NaSe6 octahedra, and an edgeedge with one SiSe4 tetrahedra. The corner-sharing octahedra tilt angles range from 3–91°. There are a spread of Na–Se bond distances ranging from 2.93–3.19 Å. In the sixth Na1+ site, Na1+ is bonded to six Se+1.75- atoms to form NaSe6 octahedra that share corners with three NaSe6 octahedra, corners with two equivalent SiSe4 tetrahedra, edges with five NaSe6 octahedra, edges with two SiSe4 tetrahedra, and edges with three equivalent NaSe5 trigonal bipyramids. The corner-sharing octahedra tilt angles range from 12–39°. There are a spread of Na–Se bond distances ranging from 3.05–3.24 Å. There are two inequivalent Si4+ sites. In the first Si4+ site, Si4+ is bonded to four Se+1.75- atoms to form SiSe4 tetrahedra that share corners with four NaSe6 octahedra, corners with two equivalent NaSe5 trigonal bipyramids, and edges with three NaSe6 octahedra. The corner-sharing octahedra tilt angles range from 19–72°. There are a spread of Si–Se bond distances ranging from 2.26–2.37 Å. In the second Si4+ site, Si4+ is bonded to four Se+1.75- atoms to form SiSe4 tetrahedra that share corners with six NaSe6 octahedra, a cornercorner with one NaSe5 trigonal bipyramid, an edgeedge with one NaSe6 octahedra, and an edgeedge with one NaSe5 trigonal bipyramid. The corner-sharing octahedra tilt angles range from 4–78°. There are a spread of Si–Se bond distances ranging from 2.27–2.36 Å. There are eight inequivalent Se+1.75- sites. In the first Se+1.75- site, Se+1.75- is bonded to four Na1+ and one Si4+ atom to form distorted SeNa4Si trigonal bipyramids that share a cornercorner with one SeNa5Si octahedra, edges with three SeNa5Si octahedra, and an edgeedge with one SeNa4Si trigonal bipyramid. The corner-sharing octahedral tilt angles are 17°. In the second Se+1.75- site, Se+1.75- is bonded in a 1-coordinate geometry to three Na1+, one Si4+, and one Se+1.75- atom. The Se–Se bond length is 2.43 Å. In the third Se+1.75- site, Se+1.75- is bonded to five Na1+ and one Si4+ atom to form distorted SeNa5Si octahedra that share corners with two SeNa5Si octahedra, edges with six SeNa5Si octahedra, and an edgeedge with one SeNa4Si trigonal bipyramid. The corner-sharing octahedra tilt angles range from 11–24°. In the fourth Se+1.75- site, Se+1.75- is bonded in a 6-coordinate geometry to five Na1+ and one Si4+ atom. In the fifth Se+1.75- site, Se+1.75- is bonded in a 1-coordinate geometry to two Na1+, one Si4+, and one Se+1.75- atom. In the sixth Se+1.75- site, Se+1.75- is bonded to five Na1+ and one Si4+ atom to form distorted SeNa5Si octahedra that share corners with two SeNa5Si octahedra, a cornercorner with one SeNa4Si trigonal bipyramid, edges with six SeNa5Si octahedra, and an edgeedge with one SeNa4Si trigonal bipyramid. The corner-sharing octahedra tilt angles range from 7–11°. In the seventh Se+1.75- site, Se+1.75- is bonded to five Na1+ and one Si4+ atom to form distorted SeNa5Si octahedra that share corners with two SeNa5Si octahedra, edges with four SeNa5Si octahedra, and an edgeedge with one SeNa4Si trigonal bipyramid. The corner-sharing octahedra tilt angles range from 7–24°. In the eighth Se+1.75- site, Se+1.75- is bonded in a 6-coordinate geometry to five Na1+ and one Si4+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on Na3SiSe4 by Materials Project. https://doi.org/10.17188/1202430

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗