Materials Data on Tb10B2Br15 by Materials Project

Abstract

Tb10B2Br15 crystallizes in the triclinic P-1 space group. The structure is three-dimensional. there are five inequivalent Tb sites. In the first Tb site, Tb is bonded to one B and five Br atoms to form TbBBr5 octahedra that share corners with four TbB2Br4 octahedra and edges with six TbBBr5 octahedra. The corner-sharing octahedra tilt angles range from 3–10°. The Tb–B bond length is 2.50 Å. There are a spread of Tb–Br bond distances ranging from 2.84–3.14 Å. In the second Tb site, Tb is bonded to one B and five Br atoms to form TbBBr5 octahedra that share corners with five TbB2Br4 octahedra and edges with six TbBBr5 octahedra. The corner-sharing octahedra tilt angles range from 0–10°. The Tb–B bond length is 2.50 Å. There are a spread of Tb–Br bond distances ranging from 2.86–3.11 Å. In the third Tb site, Tb is bonded to one B and five Br atoms to form a mixture of edge and corner-sharing TbBBr5 octahedra. The corner-sharing octahedral tilt angles are 6°. The Tb–B bond length is 2.55 Å. There are a spread of Tb–Br bond distances ranging from 2.86–3.11 Å. In the fourth Tb site, Tb is bonded to one B and five Br atoms to form a mixture of edge and corner-sharing TbBBr5 octahedra. The corner-sharing octahedra tilt angles range from 3–6°. The Tb–B bond length is 2.54 Å. There are a spread of Tb–Br bond distances ranging from 2.88–3.18 Å. In the fifth Tb site, Tb is bonded to two equivalent B and four Br atoms to form a mixture of edge and corner-sharing TbB2Br4 octahedra. The corner-sharing octahedra tilt angles range from 0–8°. There are one shorter (2.66 Å) and one longer (2.68 Å) Tb–B bond lengths. There are a spread of Tb–Br bond distances ranging from 2.95–3.10 Å. B is bonded to six Tb atoms to form edge-sharing BTb6 octahedra. There are eight inequivalent Br sites. In the first Br site, Br is bonded in a square co-planar geometry to four Tb atoms. In the second Br site, Br is bonded in a distorted T-shaped geometry to three Tb atoms. In the third Br site, Br is bonded in a distorted T-shaped geometry to three Tb atoms. In the fourth Br site, Br is bonded in a distorted T-shaped geometry to three Tb atoms. In the fifth Br site, Br is bonded in a distorted T-shaped geometry to three Tb atoms. In the sixth Br site, Br is bonded in a distorted T-shaped geometry to three Tb atoms. In the seventh Br site, Br is bonded in a rectangular see-saw-like geometry to four Tb atoms. In the eighth Br site, Br is bonded in a distorted T-shaped geometry to three Tb atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-22. Materials Data on Tb10B2Br15 by Materials Project. https://doi.org/10.17188/1204294

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗