Materials Data on BaLaTiCrO6 by Materials Project

Abstract

BaLaTiCrO6 is (Cubic) Perovskite-derived structured and crystallizes in the orthorhombic Pmma space group. The structure is three-dimensional. there are two inequivalent Ba2+ sites. In the first Ba2+ site, Ba2+ is bonded to twelve O2- atoms to form BaO12 cuboctahedra that share corners with five LaO12 cuboctahedra, corners with seven BaO12 cuboctahedra, faces with two equivalent LaO12 cuboctahedra, faces with four BaO12 cuboctahedra, faces with two equivalent CrO6 octahedra, and faces with six TiO6 octahedra. There are a spread of Ba–O bond distances ranging from 2.83–2.95 Å. In the second Ba2+ site, Ba2+ is bonded to twelve O2- atoms to form BaO12 cuboctahedra that share a cornercorner with one LaO12 cuboctahedra, corners with eleven BaO12 cuboctahedra, faces with six BaO12 cuboctahedra, and faces with eight TiO6 octahedra. There are a spread of Ba–O bond distances ranging from 2.83–2.92 Å. There are two inequivalent La3+ sites. In the first La3+ site, La3+ is bonded to twelve O2- atoms to form LaO12 cuboctahedra that share corners with five BaO12 cuboctahedra, corners with seven LaO12 cuboctahedra, faces with two equivalent BaO12 cuboctahedra, faces with four LaO12 cuboctahedra, faces with two equivalent TiO6 octahedra, and faces with six CrO6 octahedra. There are a spread of La–O bond distances ranging from 2.62–2.83 Å. In the second La3+ site, La3+ is bonded to twelve O2- atoms to form LaO12 cuboctahedra that share a cornercorner with one BaO12 cuboctahedra, corners with eleven LaO12 cuboctahedra, faces with six LaO12 cuboctahedra, and faces with eight CrO6 octahedra. There are a spread of La–O bond distances ranging from 2.56–2.88 Å. There are two inequivalent Ti4+ sites. In the first Ti4+ site, Ti4+ is bonded to six O2- atoms to form TiO6 octahedra that share corners with six TiO6 octahedra and faces with eight BaO12 cuboctahedra. The corner-sharing octahedral tilt angles are 0°. There are two shorter (1.99 Å) and four longer (2.01 Å) Ti–O bond lengths. In the second Ti4+ site, Ti4+ is bonded to six O2- atoms to form TiO6 octahedra that share corners with two equivalent CrO6 octahedra, corners with four TiO6 octahedra, faces with two equivalent LaO12 cuboctahedra, and faces with six BaO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–5°. There are a spread of Ti–O bond distances ranging from 1.95–2.03 Å. There are two inequivalent Cr3+ sites. In the first Cr3+ site, Cr3+ is bonded to six O2- atoms to form CrO6 octahedra that share corners with six CrO6 octahedra and faces with eight LaO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–4°. There are a spread of Cr–O bond distances ranging from 1.97–1.99 Å. In the second Cr3+ site, Cr3+ is bonded to six O2- atoms to form CrO6 octahedra that share corners with two equivalent TiO6 octahedra, corners with four CrO6 octahedra, faces with two equivalent BaO12 cuboctahedra, and faces with six LaO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–10°. There are a spread of Cr–O bond distances ranging from 1.98–2.01 Å. There are nine inequivalent O2- sites. In the first O2- site, O2- is bonded in a distorted linear geometry to four Ba2+ and two equivalent Ti4+ atoms. In the second O2- site, O2- is bonded in a distorted linear geometry to three Ba2+, one La3+, and two equivalent Ti4+ atoms. In the third O2- site, O2- is bonded in a 6-coordinate geometry to one Ba2+, three La3+, and two equivalent Cr3+ atoms. In the fourth O2- site, O2- is bonded in a 6-coordinate geometry to four La3+ and two equivalent Cr3+ atoms. In the fifth O2- site, O2- is bonded in a distorted linear geometry to four Ba2+ and two Ti4+ atoms. In the sixth O2- site, O2- is bonded in a distorted linear geometry to four equivalent Ba2+ and two equivalent Ti4+ atoms. In the seventh O2- site, O2- is bonded in a distorted linear geometry to four La3+ and two Cr3+ atoms. In the eighth O2- site, O2- is bonded in a distorted linear geometry to two equivalent Ba2+, two equivalent La3+, one Ti4+, and one Cr3+ atom. In the ninth O2- site, O2- is bonded in a distorted linear geometry to four equivalent La3+ and two equivalent Cr3+ atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-30. Materials Data on BaLaTiCrO6 by Materials Project. https://doi.org/10.17188/1207626

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗