Materials Data on Rb2Li14Pb3O14 by Materials Project

Abstract

Rb2Li14Pb3O14 crystallizes in the orthorhombic Immm space group. The structure is three-dimensional. Rb1+ is bonded in a 10-coordinate geometry to ten O2- atoms. There are a spread of Rb–O bond distances ranging from 3.13–3.49 Å. There are three inequivalent Li1+ sites. In the first Li1+ site, Li1+ is bonded to four O2- atoms to form LiO4 tetrahedra that share corners with four PbO6 octahedra, corners with six LiO4 tetrahedra, and edges with five LiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 23–40°. There is two shorter (1.96 Å) and two longer (1.98 Å) Li–O bond length. In the second Li1+ site, Li1+ is bonded to four O2- atoms to form distorted LiO4 tetrahedra that share corners with three PbO6 octahedra, corners with five LiO4 tetrahedra, an edgeedge with one PbO6 octahedra, and edges with three LiO4 tetrahedra. The corner-sharing octahedra tilt angles range from 3–40°. There are a spread of Li–O bond distances ranging from 1.91–2.14 Å. In the third Li1+ site, Li1+ is bonded to four O2- atoms to form distorted LiO4 tetrahedra that share a cornercorner with one PbO6 octahedra, corners with seven LiO4 tetrahedra, edges with two PbO6 octahedra, and edges with three LiO4 tetrahedra. The corner-sharing octahedral tilt angles are 67°. There are a spread of Li–O bond distances ranging from 1.97–2.18 Å. There are two inequivalent Pb4+ sites. In the first Pb4+ site, Pb4+ is bonded to six O2- atoms to form distorted PbO6 octahedra that share corners with ten LiO4 tetrahedra, an edgeedge with one PbO6 octahedra, and edges with six LiO4 tetrahedra. There are a spread of Pb–O bond distances ranging from 2.17–2.42 Å. In the second Pb4+ site, Pb4+ is bonded to six O2- atoms to form PbO6 octahedra that share corners with eight LiO4 tetrahedra, edges with two equivalent PbO6 octahedra, and edges with eight equivalent LiO4 tetrahedra. There are two shorter (2.18 Å) and four longer (2.24 Å) Pb–O bond lengths. There are four inequivalent O2- sites. In the first O2- site, O2- is bonded in a 5-coordinate geometry to one Rb1+, four Li1+, and one Pb4+ atom. In the second O2- site, O2- is bonded to six Li1+ and one Pb4+ atom to form a mixture of distorted edge and corner-sharing OLi6Pb hexagonal pyramids. In the third O2- site, O2- is bonded in a 5-coordinate geometry to two equivalent Rb1+, three Li1+, and two Pb4+ atoms. In the fourth O2- site, O2- is bonded in a 7-coordinate geometry to two equivalent Rb1+, four Li1+, and one Pb4+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-02. Materials Data on Rb2Li14Pb3O14 by Materials Project. https://doi.org/10.17188/1262069

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗