Materials Data on Na5(InTe3)2 by Materials Project

Abstract

Na5(InTe3)2 crystallizes in the orthorhombic Cmc2_1 space group. The structure is three-dimensional. there are five inequivalent Na1+ sites. In the first Na1+ site, Na1+ is bonded to six Te+1.83- atoms to form NaTe6 octahedra that share corners with eleven NaTe6 octahedra, corners with four InTe4 tetrahedra, edges with three NaTe6 octahedra, edges with two InTe4 tetrahedra, and faces with three NaTe6 octahedra. The corner-sharing octahedra tilt angles range from 18–62°. There are a spread of Na–Te bond distances ranging from 3.20–3.56 Å. In the second Na1+ site, Na1+ is bonded to six Te+1.83- atoms to form NaTe6 octahedra that share corners with eleven NaTe6 octahedra, corners with four InTe4 tetrahedra, edges with three NaTe6 octahedra, edges with two InTe4 tetrahedra, and faces with three NaTe6 octahedra. The corner-sharing octahedra tilt angles range from 20–62°. There are a spread of Na–Te bond distances ranging from 3.20–3.50 Å. In the third Na1+ site, Na1+ is bonded to six Te+1.83- atoms to form distorted NaTe6 octahedra that share corners with eleven NaTe6 octahedra, corners with five InTe4 tetrahedra, edges with three NaTe6 octahedra, an edgeedge with one InTe4 tetrahedra, and faces with three NaTe6 octahedra. The corner-sharing octahedra tilt angles range from 18–81°. There are a spread of Na–Te bond distances ranging from 3.26–3.53 Å. In the fourth Na1+ site, Na1+ is bonded to six Te+1.83- atoms to form NaTe6 octahedra that share corners with eleven NaTe6 octahedra, corners with five InTe4 tetrahedra, edges with three NaTe6 octahedra, an edgeedge with one InTe4 tetrahedra, and faces with three NaTe6 octahedra. The corner-sharing octahedra tilt angles range from 20–81°. There are a spread of Na–Te bond distances ranging from 3.28–3.45 Å. In the fifth Na1+ site, Na1+ is bonded to six Te+1.83- atoms to form distorted NaTe6 octahedra that share corners with twelve NaTe6 octahedra, edges with two equivalent NaTe6 octahedra, edges with four InTe4 tetrahedra, and faces with two NaTe6 octahedra. The corner-sharing octahedra tilt angles range from 31–81°. There are a spread of Na–Te bond distances ranging from 3.17–3.39 Å. There are four inequivalent In3+ sites. In the first In3+ site, In3+ is bonded to four Te+1.83- atoms to form InTe4 tetrahedra that share corners with ten NaTe6 octahedra, corners with two equivalent InTe4 tetrahedra, and edges with four NaTe6 octahedra. The corner-sharing octahedra tilt angles range from 41–95°. There are a spread of In–Te bond distances ranging from 2.77–2.88 Å. In the second In3+ site, In3+ is bonded to four Te+1.83- atoms to form InTe4 tetrahedra that share corners with eight NaTe6 octahedra, corners with two equivalent InTe4 tetrahedra, and edges with six NaTe6 octahedra. The corner-sharing octahedra tilt angles range from 44–61°. There are a spread of In–Te bond distances ranging from 2.78–2.88 Å. In the third In3+ site, In3+ is bonded to four Te+1.83- atoms to form InTe4 tetrahedra that share corners with ten NaTe6 octahedra, corners with two equivalent InTe4 tetrahedra, and edges with four NaTe6 octahedra. The corner-sharing octahedra tilt angles range from 41–97°. There are a spread of In–Te bond distances ranging from 2.76–2.88 Å. In the fourth In3+ site, In3+ is bonded to four Te+1.83- atoms to form InTe4 tetrahedra that share corners with eight NaTe6 octahedra, corners with two equivalent InTe4 tetrahedra, and edges with six NaTe6 octahedra. The corner-sharing octahedra tilt angles range from 45–59°. There are a spread of In–Te bond distances ranging from 2.78–2.88 Å. There are ten inequivalent Te+1.83- sites. In the first Te+1.83- site, Te+1.83- is bonded in a 6-coordinate geometry to four Na1+ and two In3+ atoms. In the second Te+1.83- site, Te+1.83- is bonded in a 6-coordinate geometry to four Na1+ and two In3+ atoms. In the third Te+1.83- site, Te+1.83- is bonded in a 7-coordinate geometry to six Na1+ and one In3+ atom. In the fourth Te+1.83- site, Te+1.83- is bonded to six Na1+ and one In3+ atom to form a mixture of distorted corner, edge, and face-sharing TeNa6In pentagonal bipyramids. In the fifth Te+1.83- site, Te+1.83- is bonded to six Na1+ and one In3+ atom to form a mixture of distorted corner, edge, and face-sharing TeNa6In pentagonal bipyramids. In the sixth Te+1.83- site, Te+1.83- is bonded in a 7-coordinate geometry to six Na1+ and one In3+ atom. In the seventh Te+1.83- site, Te+1.83- is bonded in a 5-coordinate geometry to four Na1+ and one In3+ atom. In the eighth Te+1.83- site, Te+1.83- is bonded to six Na1+ and one In3+ atom to form a mixture of distorted corner, edge, and face-sharing TeNa6In pentagonal bipyramids. In the ninth Te+1.83- site, Te+1.83- is bonded to six Na1+ and one In3+ atom to form a mixture of distorted corner, edge, and face-sharing TeNa6In pentagonal bipyramids. In the tenth Te+1.83- site, Te+1.83- is bonded in a 5-coordinate geometry to four Na1+ and one In3+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-30. Materials Data on Na5(InTe3)2 by Materials Project. https://doi.org/10.17188/1262215

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗