Materials Data on GdAl22O34 by Materials Project

Abstract

GdAl22O34 crystallizes in the triclinic P-1 space group. The structure is three-dimensional. Gd is bonded in a 8-coordinate geometry to eight O atoms. There are a spread of Gd–O bond distances ranging from 2.41–2.87 Å. There are twelve inequivalent Al sites. In the first Al site, Al is bonded to six O atoms to form AlO6 octahedra that share corners with six AlO4 tetrahedra and edges with six AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.90–1.92 Å. In the second Al site, Al is bonded to six O atoms to form AlO6 octahedra that share corners with five AlO4 tetrahedra and edges with five AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.82–2.09 Å. In the third Al site, Al is bonded to six O atoms to form AlO6 octahedra that share corners with five AlO4 tetrahedra and edges with five AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.81–2.09 Å. In the fourth Al site, Al is bonded to six O atoms to form AlO6 octahedra that share corners with five AlO4 tetrahedra and edges with five AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.81–2.08 Å. In the fifth Al site, Al is bonded to six O atoms to form AlO6 octahedra that share corners with six AlO4 tetrahedra and edges with six AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.90–1.92 Å. In the sixth Al site, Al is bonded to four O atoms to form corner-sharing AlO4 tetrahedra. The corner-sharing octahedra tilt angles range from 53–59°. There is two shorter (1.81 Å) and two longer (1.83 Å) Al–O bond length. In the seventh Al site, Al is bonded to four O atoms to form AlO4 tetrahedra that share corners with six AlO6 octahedra and a cornercorner with one AlO4 tetrahedra. The corner-sharing octahedra tilt angles range from 53–58°. There are a spread of Al–O bond distances ranging from 1.74–1.81 Å. In the eighth Al site, Al is bonded to four O atoms to form AlO4 tetrahedra that share corners with six AlO6 octahedra and a cornercorner with one AlO4 tetrahedra. The corner-sharing octahedra tilt angles range from 53–57°. There are a spread of Al–O bond distances ranging from 1.73–1.82 Å. In the ninth Al site, Al is bonded to six O atoms to form AlO6 octahedra that share corners with five AlO4 tetrahedra and edges with five AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.81–2.06 Å. In the tenth Al site, Al is bonded to six O atoms to form AlO6 octahedra that share corners with five AlO4 tetrahedra and edges with five AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.85–1.99 Å. In the eleventh Al site, Al is bonded to six O atoms to form AlO6 octahedra that share corners with five AlO4 tetrahedra and edges with five AlO6 octahedra. There are a spread of Al–O bond distances ranging from 1.82–2.08 Å. In the twelfth Al site, Al is bonded to four O atoms to form corner-sharing AlO4 tetrahedra. The corner-sharing octahedra tilt angles range from 52–60°. There are a spread of Al–O bond distances ranging from 1.81–1.83 Å. There are seventeen inequivalent O sites. In the first O site, O is bonded in a trigonal non-coplanar geometry to three Al atoms. In the second O site, O is bonded in a rectangular see-saw-like geometry to four Al atoms. In the third O site, O is bonded in a rectangular see-saw-like geometry to four Al atoms. In the fourth O site, O is bonded in a rectangular see-saw-like geometry to four Al atoms. In the fifth O site, O is bonded in a rectangular see-saw-like geometry to four Al atoms. In the sixth O site, O is bonded in a 3-coordinate geometry to one Gd and three Al atoms. In the seventh O site, O is bonded in a distorted trigonal planar geometry to one Gd and three Al atoms. In the eighth O site, O is bonded in a trigonal planar geometry to three Al atoms. In the ninth O site, O is bonded in a trigonal planar geometry to three Al atoms. In the tenth O site, O is bonded in a 3-coordinate geometry to one Gd and two Al atoms. In the eleventh O site, O is bonded in a distorted trigonal planar geometry to one Gd and three Al atoms. In the twelfth O site, O is bonded in a trigonal planar geometry to three Al atoms. In the thirteenth O site, O is bonded in a trigonal planar geometry to three Al atoms. In the fourteenth O site, O is bonded in a rectangular see-saw-like geometry to four Al atoms. In the fifteenth O site, O is bonded in a rectangular see-saw-like geometry to four Al atoms. In the sixteenth O site, O is bonded in a rectangular see-saw-like geometry to four Al atoms. In the seventeenth O site, O is bonded in a rectangular see-saw-like geometry to four Al atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-02. Materials Data on GdAl22O34 by Materials Project. https://doi.org/10.17188/1263251

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗