Materials Data on U7(Te12O35)2 by Materials Project

Abstract

U7(Te12O35)2 crystallizes in the trigonal R-3 space group. The structure is three-dimensional. there are three inequivalent U sites. In the first U site, U is bonded to eight O atoms to form distorted UO8 hexagonal bipyramids that share edges with two equivalent TeO5 square pyramids. There are a spread of U–O bond distances ranging from 1.83–2.51 Å. In the second U site, U is bonded to eight O atoms to form distorted UO8 hexagonal bipyramids that share edges with six equivalent TeO5 square pyramids. There are two shorter (1.83 Å) and six longer (2.46 Å) U–O bond lengths. In the third U site, U is bonded to eight O atoms to form distorted UO8 hexagonal bipyramids that share edges with four TeO5 square pyramids. There are a spread of U–O bond distances ranging from 1.83–2.48 Å. There are four inequivalent Te sites. In the first Te site, Te is bonded to five O atoms to form distorted TeO5 square pyramids that share corners with three TeO5 square pyramids and edges with two UO8 hexagonal bipyramids. There are a spread of Te–O bond distances ranging from 1.91–2.40 Å. In the second Te site, Te is bonded in a 5-coordinate geometry to five O atoms. There are a spread of Te–O bond distances ranging from 1.91–2.66 Å. In the third Te site, Te is bonded in a 5-coordinate geometry to five O atoms. There are a spread of Te–O bond distances ranging from 1.92–2.48 Å. In the fourth Te site, Te is bonded to five O atoms to form distorted TeO5 square pyramids that share corners with three TeO5 square pyramids and edges with two UO8 hexagonal bipyramids. There are a spread of Te–O bond distances ranging from 1.92–2.40 Å. There are thirteen inequivalent O sites. In the first O site, O is bonded in a single-bond geometry to one U atom. In the second O site, O is bonded in a single-bond geometry to one U atom. In the third O site, O is bonded in a distorted trigonal planar geometry to one U and two Te atoms. In the fourth O site, O is bonded in a distorted trigonal planar geometry to one U and two Te atoms. In the fifth O site, O is bonded in a distorted trigonal non-coplanar geometry to one U and two Te atoms. In the sixth O site, O is bonded in a distorted trigonal planar geometry to one U and two Te atoms. In the seventh O site, O is bonded in a trigonal planar geometry to three equivalent Te atoms. In the eighth O site, O is bonded in a distorted bent 120 degrees geometry to three Te atoms. In the ninth O site, O is bonded in a distorted trigonal planar geometry to one U and two equivalent Te atoms. In the tenth O site, O is bonded in a single-bond geometry to one U atom. In the eleventh O site, O is bonded in a distorted trigonal planar geometry to one U and two Te atoms. In the twelfth O site, O is bonded in a distorted trigonal planar geometry to one U and two Te atoms. In the thirteenth O site, O is bonded in a bent 120 degrees geometry to two equivalent Te atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on U7(Te12O35)2 by Materials Project. https://doi.org/10.17188/1263261

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗