Materials Data on Li5V5Cl16 by Materials Project

Abstract

Li5V5Cl16 is beta indium sulfide-derived structured and crystallizes in the orthorhombic Aem2 space group. The structure is three-dimensional. there are four inequivalent Li1+ sites. In the first Li1+ site, Li1+ is bonded to four Cl1- atoms to form LiCl4 tetrahedra that share corners with five LiCl6 octahedra and corners with seven VCl6 octahedra. The corner-sharing octahedra tilt angles range from 56–61°. There are a spread of Li–Cl bond distances ranging from 2.34–2.57 Å. In the second Li1+ site, Li1+ is bonded to six Cl1- atoms to form LiCl6 octahedra that share corners with three LiCl4 tetrahedra and edges with six VCl6 octahedra. There are a spread of Li–Cl bond distances ranging from 2.52–2.63 Å. In the third Li1+ site, Li1+ is bonded to six Cl1- atoms to form LiCl6 octahedra that share corners with three LiCl4 tetrahedra, edges with two equivalent LiCl6 octahedra, and edges with four VCl6 octahedra. There are a spread of Li–Cl bond distances ranging from 2.48–2.68 Å. In the fourth Li1+ site, Li1+ is bonded to four Cl1- atoms to form LiCl4 tetrahedra that share corners with four LiCl6 octahedra and corners with eight VCl6 octahedra. The corner-sharing octahedra tilt angles range from 56–62°. All Li–Cl bond lengths are 2.41 Å. There are three inequivalent V+2.20+ sites. In the first V+2.20+ site, V+2.20+ is bonded to six Cl1- atoms to form VCl6 octahedra that share corners with three LiCl4 tetrahedra, edges with three LiCl6 octahedra, and edges with three VCl6 octahedra. There are a spread of V–Cl bond distances ranging from 2.44–2.52 Å. In the second V+2.20+ site, V+2.20+ is bonded to six Cl1- atoms to form VCl6 octahedra that share corners with three LiCl4 tetrahedra, edges with two equivalent LiCl6 octahedra, and edges with four VCl6 octahedra. There are a spread of V–Cl bond distances ranging from 2.44–2.53 Å. In the third V+2.20+ site, V+2.20+ is bonded to six Cl1- atoms to form VCl6 octahedra that share corners with three LiCl4 tetrahedra, edges with three LiCl6 octahedra, and edges with three VCl6 octahedra. There are a spread of V–Cl bond distances ranging from 2.38–2.57 Å. There are ten inequivalent Cl1- sites. In the first Cl1- site, Cl1- is bonded in a distorted T-shaped geometry to one Li1+ and two equivalent V+2.20+ atoms. In the second Cl1- site, Cl1- is bonded in a distorted T-shaped geometry to one Li1+ and two V+2.20+ atoms. In the third Cl1- site, Cl1- is bonded in a distorted T-shaped geometry to three V+2.20+ atoms. In the fourth Cl1- site, Cl1- is bonded to one Li1+ and three V+2.20+ atoms to form distorted ClLiV3 trigonal pyramids that share corners with two equivalent ClLi3V tetrahedra, a cornercorner with one ClLi2V2 trigonal pyramid, and edges with three ClLi2V2 trigonal pyramids. In the fifth Cl1- site, Cl1- is bonded in a distorted T-shaped geometry to one Li1+ and two equivalent V+2.20+ atoms. In the sixth Cl1- site, Cl1- is bonded to two Li1+ and two V+2.20+ atoms to form distorted ClLi2V2 trigonal pyramids that share a cornercorner with one ClLi2V2 trigonal pyramid and edges with three ClLiV3 trigonal pyramids. In the seventh Cl1- site, Cl1- is bonded in a distorted T-shaped geometry to two equivalent Li1+ and one V+2.20+ atom. In the eighth Cl1- site, Cl1- is bonded to two Li1+ and two equivalent V+2.20+ atoms to form distorted ClLi2V2 trigonal pyramids that share corners with two equivalent ClLi3V tetrahedra, a cornercorner with one ClLiV3 trigonal pyramid, and edges with three ClLiV3 trigonal pyramids. In the ninth Cl1- site, Cl1- is bonded in a rectangular see-saw-like geometry to two Li1+ and two equivalent V+2.20+ atoms. In the tenth Cl1- site, Cl1- is bonded to three Li1+ and one V+2.20+ atom to form distorted ClLi3V tetrahedra that share a cornercorner with one ClLi3V tetrahedra, corners with two ClLiV3 trigonal pyramids, and an edgeedge with one ClLi3V tetrahedra.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on Li5V5Cl16 by Materials Project. https://doi.org/10.17188/1263445

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗