Materials Data on Er2Ni12As7 by Materials Project

Abstract

Er2Ni12As7 crystallizes in the hexagonal P-6 space group. The structure is three-dimensional. there are two inequivalent Er3+ sites. In the first Er3+ site, Er3+ is bonded to six equivalent As3- atoms to form distorted ErAs6 pentagonal pyramids that share corners with six equivalent NiAs5 square pyramids, corners with twelve NiAs4 tetrahedra, edges with three equivalent NiAs5 square pyramids, edges with nine NiAs4 tetrahedra, and faces with two equivalent ErAs6 pentagonal pyramids. All Er–As bond lengths are 2.95 Å. In the second Er3+ site, Er3+ is bonded to six equivalent As3- atoms to form distorted ErAs6 pentagonal pyramids that share corners with six equivalent NiAs5 square pyramids, corners with twelve NiAs4 tetrahedra, edges with twelve NiAs4 tetrahedra, and faces with two equivalent ErAs6 pentagonal pyramids. All Er–As bond lengths are 2.96 Å. There are four inequivalent Ni+1.25+ sites. In the first Ni+1.25+ site, Ni+1.25+ is bonded to four As3- atoms to form NiAs4 tetrahedra that share corners with two equivalent ErAs6 pentagonal pyramids, corners with two equivalent NiAs5 square pyramids, corners with twelve NiAs4 tetrahedra, edges with three ErAs6 pentagonal pyramids, edges with two equivalent NiAs5 square pyramids, and edges with three NiAs4 tetrahedra. There are a spread of Ni–As bond distances ranging from 2.32–2.40 Å. In the second Ni+1.25+ site, Ni+1.25+ is bonded to four As3- atoms to form NiAs4 tetrahedra that share corners with four ErAs6 pentagonal pyramids, corners with two equivalent NiAs5 square pyramids, corners with ten NiAs4 tetrahedra, an edgeedge with one ErAs6 pentagonal pyramid, edges with four equivalent NiAs5 square pyramids, and edges with three NiAs4 tetrahedra. There are a spread of Ni–As bond distances ranging from 2.27–2.38 Å. In the third Ni+1.25+ site, Ni+1.25+ is bonded to four As3- atoms to form NiAs4 tetrahedra that share corners with two equivalent ErAs6 pentagonal pyramids, corners with four equivalent NiAs5 square pyramids, corners with ten NiAs4 tetrahedra, edges with three ErAs6 pentagonal pyramids, an edgeedge with one NiAs5 square pyramid, and edges with four NiAs4 tetrahedra. There are a spread of Ni–As bond distances ranging from 2.35–2.42 Å. In the fourth Ni+1.25+ site, Ni+1.25+ is bonded to five As3- atoms to form distorted NiAs5 square pyramids that share corners with four ErAs6 pentagonal pyramids, corners with four equivalent NiAs5 square pyramids, corners with eight NiAs4 tetrahedra, an edgeedge with one ErAs6 pentagonal pyramid, edges with four equivalent NiAs5 square pyramids, and edges with seven NiAs4 tetrahedra. There are a spread of Ni–As bond distances ranging from 2.43–2.62 Å. There are three inequivalent As3- sites. In the first As3- site, As3- is bonded in a 9-coordinate geometry to nine Ni+1.25+ atoms. In the second As3- site, As3- is bonded in a 9-coordinate geometry to two equivalent Er3+ and seven Ni+1.25+ atoms. In the third As3- site, As3- is bonded in a 9-coordinate geometry to two equivalent Er3+ and seven Ni+1.25+ atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-18. Materials Data on Er2Ni12As7 by Materials Project. https://doi.org/10.17188/1266644

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗