Materials Data on Ba4Eu4Zn3PtO15 by Materials Project

Abstract

Ba4Eu4PtZn3O15 crystallizes in the hexagonal P6_3mc space group. The structure is three-dimensional. there are two inequivalent Ba2+ sites. In the first Ba2+ site, Ba2+ is bonded to twelve O2- atoms to form distorted BaO12 cuboctahedra that share faces with two equivalent PtO6 octahedra and faces with three equivalent ZnO4 tetrahedra. There are a spread of Ba–O bond distances ranging from 2.78–3.24 Å. In the second Ba2+ site, Ba2+ is bonded in a 10-coordinate geometry to ten O2- atoms. There are a spread of Ba–O bond distances ranging from 2.79–3.33 Å. There are two inequivalent Eu3+ sites. In the first Eu3+ site, Eu3+ is bonded in a 8-coordinate geometry to eight O2- atoms. There are a spread of Eu–O bond distances ranging from 2.33–2.74 Å. In the second Eu3+ site, Eu3+ is bonded to six equivalent O2- atoms to form distorted EuO6 octahedra that share corners with six equivalent ZnO4 tetrahedra and faces with two equivalent EuO6 octahedra. There are three shorter (2.34 Å) and three longer (2.52 Å) Eu–O bond lengths. Pt4+ is bonded to six O2- atoms to form PtO6 octahedra that share corners with three equivalent ZnO4 tetrahedra and faces with two equivalent BaO12 cuboctahedra. There are three shorter (2.01 Å) and three longer (2.04 Å) Pt–O bond lengths. Zn2+ is bonded to four O2- atoms to form ZnO4 tetrahedra that share a cornercorner with one PtO6 octahedra, corners with two equivalent EuO6 octahedra, and a faceface with one BaO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 3–68°. There are a spread of Zn–O bond distances ranging from 1.93–2.07 Å. There are four inequivalent O2- sites. In the first O2- site, O2- is bonded in a 2-coordinate geometry to three Ba2+, two equivalent Eu3+, and one Zn2+ atom. In the second O2- site, O2- is bonded in a 3-coordinate geometry to three equivalent Ba2+, two equivalent Eu3+, and one Zn2+ atom. In the third O2- site, O2- is bonded to three Ba2+, two equivalent Eu3+, and one Pt4+ atom to form a mixture of distorted face and corner-sharing OBa3Eu2Pt octahedra. The corner-sharing octahedra tilt angles range from 2–62°. In the fourth O2- site, O2- is bonded to two Ba2+, two equivalent Eu3+, one Pt4+, and one Zn2+ atom to form a mixture of distorted face and corner-sharing OBa2Eu2ZnPt octahedra. The corner-sharing octahedra tilt angles range from 2–62°.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-15. Materials Data on Ba4Eu4Zn3PtO15 by Materials Project. https://doi.org/10.17188/1271601

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗