Materials Data on Fe2BO4 by Materials Project

Abstract

Fe2BO4 crystallizes in the monoclinic Pc space group. The structure is three-dimensional. there are eight inequivalent Fe+2.50+ sites. In the first Fe+2.50+ site, Fe+2.50+ is bonded to six O2- atoms to form a mixture of edge and corner-sharing FeO6 octahedra. The corner-sharing octahedra tilt angles range from 57–64°. There are a spread of Fe–O bond distances ranging from 1.94–2.18 Å. In the second Fe+2.50+ site, Fe+2.50+ is bonded to six O2- atoms to form a mixture of edge and corner-sharing FeO6 octahedra. The corner-sharing octahedra tilt angles range from 59–66°. There are a spread of Fe–O bond distances ranging from 2.07–2.29 Å. In the third Fe+2.50+ site, Fe+2.50+ is bonded to six O2- atoms to form a mixture of edge and corner-sharing FeO6 octahedra. The corner-sharing octahedra tilt angles range from 54–60°. There are a spread of Fe–O bond distances ranging from 1.96–2.22 Å. In the fourth Fe+2.50+ site, Fe+2.50+ is bonded to six O2- atoms to form a mixture of edge and corner-sharing FeO6 octahedra. The corner-sharing octahedra tilt angles range from 53–66°. There are a spread of Fe–O bond distances ranging from 1.98–2.15 Å. In the fifth Fe+2.50+ site, Fe+2.50+ is bonded to six O2- atoms to form a mixture of edge and corner-sharing FeO6 octahedra. The corner-sharing octahedra tilt angles range from 54–66°. There are a spread of Fe–O bond distances ranging from 2.04–2.31 Å. In the sixth Fe+2.50+ site, Fe+2.50+ is bonded to six O2- atoms to form a mixture of edge and corner-sharing FeO6 octahedra. The corner-sharing octahedra tilt angles range from 53–61°. There are a spread of Fe–O bond distances ranging from 1.98–2.18 Å. In the seventh Fe+2.50+ site, Fe+2.50+ is bonded to six O2- atoms to form a mixture of edge and corner-sharing FeO6 octahedra. The corner-sharing octahedra tilt angles range from 57–66°. There are a spread of Fe–O bond distances ranging from 2.08–2.27 Å. In the eighth Fe+2.50+ site, Fe+2.50+ is bonded to six O2- atoms to form a mixture of edge and corner-sharing FeO6 octahedra. The corner-sharing octahedra tilt angles range from 59–65°. There are a spread of Fe–O bond distances ranging from 2.03–2.33 Å. There are four inequivalent B3+ sites. In the first B3+ site, B3+ is bonded in a trigonal planar geometry to three O2- atoms. There are a spread of B–O bond distances ranging from 1.37–1.41 Å. In the second B3+ site, B3+ is bonded in a trigonal planar geometry to three O2- atoms. There is one shorter (1.38 Å) and two longer (1.40 Å) B–O bond length. In the third B3+ site, B3+ is bonded in a trigonal planar geometry to three O2- atoms. There is one shorter (1.37 Å) and two longer (1.40 Å) B–O bond length. In the fourth B3+ site, B3+ is bonded in a trigonal planar geometry to three O2- atoms. There is one shorter (1.38 Å) and two longer (1.40 Å) B–O bond length. There are sixteen inequivalent O2- sites. In the first O2- site, O2- is bonded in a 1-coordinate geometry to three Fe+2.50+ and one B3+ atom. In the second O2- site, O2- is bonded in a distorted trigonal planar geometry to two Fe+2.50+ and one B3+ atom. In the third O2- site, O2- is bonded to four Fe+2.50+ atoms to form distorted edge-sharing OFe4 trigonal pyramids. In the fourth O2- site, O2- is bonded in a 1-coordinate geometry to three Fe+2.50+ and one B3+ atom. In the fifth O2- site, O2- is bonded in a 1-coordinate geometry to three Fe+2.50+ and one B3+ atom. In the sixth O2- site, O2- is bonded to four Fe+2.50+ atoms to form a mixture of distorted edge and corner-sharing OFe4 tetrahedra. In the seventh O2- site, O2- is bonded in a distorted trigonal planar geometry to two Fe+2.50+ and one B3+ atom. In the eighth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to three Fe+2.50+ and one B3+ atom. In the ninth O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to three Fe+2.50+ and one B3+ atom. In the tenth O2- site, O2- is bonded in a distorted trigonal planar geometry to two Fe+2.50+ and one B3+ atom. In the eleventh O2- site, O2- is bonded in a distorted rectangular see-saw-like geometry to four Fe+2.50+ atoms. In the twelfth O2- site, O2- is bonded in a 1-coordinate geometry to three Fe+2.50+ and one B3+ atom. In the thirteenth O2- site, O2- is bonded in a 1-coordinate geometry to three Fe+2.50+ and one B3+ atom. In the fourteenth O2- site, O2- is bonded to four Fe+2.50+ atoms to form a mixture of distorted edge and corner-sharing OFe4 tetrahedra. In the fifteenth O2- site, O2- is bonded in a distorted trigonal planar geometry to two Fe+2.50+ and one B3+ atom. In the sixteenth O2- site, O2- is bonded in a 1-coordinate geometry to three Fe+2.50+ and one B3+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-08-03. Materials Data on Fe2BO4 by Materials Project. https://doi.org/10.17188/1273525

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗