Materials Data on Rb5Sn(PSe5)3 by Materials Project

Abstract

Rb5Sn(PSe5)3 crystallizes in the triclinic P-1 space group. The structure is three-dimensional. there are five inequivalent Rb1+ sites. In the first Rb1+ site, Rb1+ is bonded in a 9-coordinate geometry to nine Se+1.60- atoms. There are a spread of Rb–Se bond distances ranging from 3.55–4.07 Å. In the second Rb1+ site, Rb1+ is bonded in a 8-coordinate geometry to eight Se+1.60- atoms. There are a spread of Rb–Se bond distances ranging from 3.46–4.09 Å. In the third Rb1+ site, Rb1+ is bonded in a 8-coordinate geometry to eight Se+1.60- atoms. There are a spread of Rb–Se bond distances ranging from 3.50–3.88 Å. In the fourth Rb1+ site, Rb1+ is bonded to eight Se+1.60- atoms to form RbSe8 hexagonal bipyramids that share corners with two equivalent RbSe8 hexagonal bipyramids, a cornercorner with one SnSe6 octahedra, a cornercorner with one PSe4 tetrahedra, an edgeedge with one RbSe8 hexagonal bipyramid, and edges with three PSe4 tetrahedra. The corner-sharing octahedral tilt angles are 32°. There are a spread of Rb–Se bond distances ranging from 3.47–3.94 Å. In the fifth Rb1+ site, Rb1+ is bonded in a 7-coordinate geometry to seven Se+1.60- atoms. There are a spread of Rb–Se bond distances ranging from 3.45–3.94 Å. Sn4+ is bonded to six Se+1.60- atoms to form SnSe6 octahedra that share a cornercorner with one RbSe8 hexagonal bipyramid and corners with three PSe4 tetrahedra. There are a spread of Sn–Se bond distances ranging from 2.73–2.84 Å. There are three inequivalent P5+ sites. In the first P5+ site, P5+ is bonded to four Se+1.60- atoms to form PSe4 tetrahedra that share a cornercorner with one RbSe8 hexagonal bipyramid, a cornercorner with one SnSe6 octahedra, and an edgeedge with one RbSe8 hexagonal bipyramid. The corner-sharing octahedral tilt angles are 71°. There are a spread of P–Se bond distances ranging from 2.18–2.32 Å. In the second P5+ site, P5+ is bonded to four Se+1.60- atoms to form PSe4 tetrahedra that share a cornercorner with one SnSe6 octahedra. The corner-sharing octahedral tilt angles are 74°. There are a spread of P–Se bond distances ranging from 2.17–2.33 Å. In the third P5+ site, P5+ is bonded to four Se+1.60- atoms to form PSe4 tetrahedra that share a cornercorner with one SnSe6 octahedra and edges with two equivalent RbSe8 hexagonal bipyramids. The corner-sharing octahedral tilt angles are 74°. There are a spread of P–Se bond distances ranging from 2.18–2.32 Å. There are fifteen inequivalent Se+1.60- sites. In the first Se+1.60- site, Se+1.60- is bonded in a 1-coordinate geometry to one Rb1+, one P5+, and one Se+1.60- atom. The Se–Se bond length is 2.34 Å. In the second Se+1.60- site, Se+1.60- is bonded in a distorted rectangular see-saw-like geometry to two Rb1+, one Sn4+, and one Se+1.60- atom. In the third Se+1.60- site, Se+1.60- is bonded in a 2-coordinate geometry to two Rb1+, one Sn4+, and one P5+ atom. In the fourth Se+1.60- site, Se+1.60- is bonded in a 5-coordinate geometry to four Rb1+ and one P5+ atom. In the fifth Se+1.60- site, Se+1.60- is bonded in a 5-coordinate geometry to three Rb1+, one Sn4+, and one Se+1.60- atom. The Se–Se bond length is 2.38 Å. In the sixth Se+1.60- site, Se+1.60- is bonded in a 5-coordinate geometry to four Rb1+ and one P5+ atom. In the seventh Se+1.60- site, Se+1.60- is bonded in a 2-coordinate geometry to two Rb1+, one Sn4+, and one P5+ atom. In the eighth Se+1.60- site, Se+1.60- is bonded in a 4-coordinate geometry to two Rb1+, one Sn4+, and one P5+ atom. In the ninth Se+1.60- site, Se+1.60- is bonded in a 1-coordinate geometry to four Rb1+ and one P5+ atom. In the tenth Se+1.60- site, Se+1.60- is bonded in a 1-coordinate geometry to four Rb1+ and one P5+ atom. In the eleventh Se+1.60- site, Se+1.60- is bonded in a 1-coordinate geometry to four Rb1+ and one P5+ atom. In the twelfth Se+1.60- site, Se+1.60- is bonded in a 1-coordinate geometry to four Rb1+ and one P5+ atom. In the thirteenth Se+1.60- site, Se+1.60- is bonded in a distorted single-bond geometry to one Rb1+, one P5+, and one Se+1.60- atom. The Se–Se bond length is 2.36 Å. In the fourteenth Se+1.60- site, Se+1.60- is bonded in a 1-coordinate geometry to one Rb1+, one Sn4+, and one Se+1.60- atom. In the fifteenth Se+1.60- site, Se+1.60- is bonded in a distorted single-bond geometry to two Rb1+, one P5+, and one Se+1.60- atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-15. Materials Data on Rb5Sn(PSe5)3 by Materials Project. https://doi.org/10.17188/1276152

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗