Materials Data on Ba(Cu5P2)2 by Materials Project

Abstract

Ba(Cu5P2)2 crystallizes in the monoclinic C2/m space group. The structure is three-dimensional. Ba2+ is bonded in a 7-coordinate geometry to seven P3- atoms. There are a spread of Ba–P bond distances ranging from 3.18–3.33 Å. There are ten inequivalent Cu1+ sites. In the first Cu1+ site, Cu1+ is bonded in a 3-coordinate geometry to three P3- atoms. There are one shorter (2.26 Å) and two longer (2.41 Å) Cu–P bond lengths. In the second Cu1+ site, Cu1+ is bonded in a distorted trigonal non-coplanar geometry to three P3- atoms. There are one shorter (2.32 Å) and two longer (2.41 Å) Cu–P bond lengths. In the third Cu1+ site, Cu1+ is bonded in a bent 120 degrees geometry to two P3- atoms. There are one shorter (2.38 Å) and one longer (2.42 Å) Cu–P bond lengths. In the fourth Cu1+ site, Cu1+ is bonded in a distorted water-like geometry to three P3- atoms. There are two shorter (2.37 Å) and one longer (2.91 Å) Cu–P bond lengths. In the fifth Cu1+ site, Cu1+ is bonded in a bent 120 degrees geometry to two equivalent P3- atoms. Both Cu–P bond lengths are 2.33 Å. In the sixth Cu1+ site, Cu1+ is bonded in a distorted bent 150 degrees geometry to two P3- atoms. There are one shorter (2.31 Å) and one longer (2.33 Å) Cu–P bond lengths. In the seventh Cu1+ site, Cu1+ is bonded in a distorted trigonal non-coplanar geometry to three P3- atoms. There are one shorter (2.36 Å) and two longer (2.43 Å) Cu–P bond lengths. In the eighth Cu1+ site, Cu1+ is bonded in a 3-coordinate geometry to three P3- atoms. There are one shorter (2.28 Å) and two longer (2.50 Å) Cu–P bond lengths. In the ninth Cu1+ site, Cu1+ is bonded to four P3- atoms to form a mixture of distorted corner and edge-sharing CuP4 tetrahedra. There are a spread of Cu–P bond distances ranging from 2.38–2.54 Å. In the tenth Cu1+ site, Cu1+ is bonded in a distorted trigonal planar geometry to three P3- atoms. There are two shorter (2.33 Å) and one longer (2.40 Å) Cu–P bond lengths. There are four inequivalent P3- sites. In the first P3- site, P3- is bonded in a 9-coordinate geometry to two equivalent Ba2+ and seven Cu1+ atoms. In the second P3- site, P3- is bonded in a 7-coordinate geometry to two equivalent Ba2+ and eight Cu1+ atoms. In the third P3- site, P3- is bonded in a 9-coordinate geometry to two equivalent Ba2+ and seven Cu1+ atoms. In the fourth P3- site, P3- is bonded in a 7-coordinate geometry to one Ba2+ and six Cu1+ atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-23. Materials Data on Ba(Cu5P2)2 by Materials Project. https://doi.org/10.17188/1277949

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗