Materials Data on LaSe by Materials Project

View original source ↗Read source document ↗Export metadata ↓

Abstract

LaSe is BCT5-derived structured and crystallizes in the triclinic P1 space group. The structure is two-dimensional and consists of two LaSe sheets oriented in the (0, 0, 1) direction. there are two inequivalent La2+ sites. In the first La2+ site, La2+ is bonded to five Se2- atoms to form a mixture of distorted corner and edge-sharing LaSe5 square pyramids. There are four shorter (3.02 Å) and one longer (3.06 Å) La–Se bond lengths. In the second La2+ site, La2+ is bonded to five Se2- atoms to form a mixture of distorted corner and edge-sharing LaSe5 square pyramids. There are four shorter (3.02 Å) and one longer (3.06 Å) La–Se bond lengths. There are two inequivalent Se2- sites. In the first Se2- site, Se2- is bonded to five La2+ atoms to form a mixture of distorted corner and edge-sharing SeLa5 square pyramids. In the second Se2- site, Se2- is bonded to five La2+ atoms to form a mixture of distorted corner and edge-sharing SeLa5 square pyramids.

Explore related subjects

36 MATERIALS SCIENCEcrystal structureLa-SeLaSe

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-15. Materials Data on LaSe by Materials Project. https://doi.org/10.17188/1280221

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗