Materials Data on SbTe(SeF3)2 by Materials Project

Abstract

SbTe(SeF3)2 crystallizes in the orthorhombic P2_12_12_1 space group. The structure is three-dimensional. there are two inequivalent Sb5+ sites. In the first Sb5+ site, Sb5+ is bonded in a rectangular see-saw-like geometry to four F1- atoms. There are a spread of Sb–F bond distances ranging from 1.91–2.16 Å. In the second Sb5+ site, Sb5+ is bonded in a distorted L-shaped geometry to one Se+1.50- and two F1- atoms. The Sb–Se bond length is 3.11 Å. There are one shorter (1.96 Å) and one longer (2.36 Å) Sb–F bond lengths. There are two inequivalent Te4+ sites. In the first Te4+ site, Te4+ is bonded in a single-bond geometry to one Se+1.50- and one F1- atom. The Te–Se bond length is 2.90 Å. The Te–F bond length is 2.05 Å. In the second Te4+ site, Te4+ is bonded in a distorted T-shaped geometry to one Se+1.50- and three F1- atoms. The Te–Se bond length is 2.61 Å. There are a spread of Te–F bond distances ranging from 1.95–2.02 Å. There are four inequivalent Se+1.50- sites. In the first Se+1.50- site, Se+1.50- is bonded in a 9-coordinate geometry to one Sb5+, one Te4+, one Se+1.50-, and six F1- atoms. The Se–Se bond length is 2.41 Å. There are a spread of Se–F bond distances ranging from 2.94–3.40 Å. In the second Se+1.50- site, Se+1.50- is bonded in a 4-coordinate geometry to four F1- atoms. There are a spread of Se–F bond distances ranging from 1.80–2.30 Å. In the third Se+1.50- site, Se+1.50- is bonded in a 6-coordinate geometry to one Te4+, two Se+1.50-, and three F1- atoms. The Se–Se bond length is 2.35 Å. There are a spread of Se–F bond distances ranging from 3.21–3.30 Å. In the fourth Se+1.50- site, Se+1.50- is bonded in a distorted single-bond geometry to one Se+1.50- and one F1- atom. The Se–F bond length is 1.83 Å. There are twelve inequivalent F1- sites. In the first F1- site, F1- is bonded in a single-bond geometry to one Te4+ and one Se+1.50- atom. In the second F1- site, F1- is bonded in a single-bond geometry to one Te4+ atom. In the third F1- site, F1- is bonded in a 2-coordinate geometry to one Sb5+ and two Se+1.50- atoms. In the fourth F1- site, F1- is bonded in a single-bond geometry to two Se+1.50- atoms. In the fifth F1- site, F1- is bonded in a single-bond geometry to two Se+1.50- atoms. In the sixth F1- site, F1- is bonded in a 2-coordinate geometry to one Sb5+ and two Se+1.50- atoms. In the seventh F1- site, F1- is bonded in a distorted single-bond geometry to one Sb5+ and one Se+1.50- atom. In the eighth F1- site, F1- is bonded in a single-bond geometry to one Te4+ and one Se+1.50- atom. In the ninth F1- site, F1- is bonded in a single-bond geometry to one Se+1.50- atom. In the tenth F1- site, F1- is bonded in a single-bond geometry to one Sb5+ and one Se+1.50- atom. In the eleventh F1- site, F1- is bonded in a distorted single-bond geometry to one Te4+ and one Se+1.50- atom. In the twelfth F1- site, F1- is bonded in a linear geometry to two Sb5+ atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-29. Materials Data on SbTe(SeF3)2 by Materials Project. https://doi.org/10.17188/1281448

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗