Materials Data on CuGe2P3 by Materials Project

Abstract

CuGe2P3 crystallizes in the monoclinic Cm space group. The structure is two-dimensional and consists of two CuGe2P3 sheets oriented in the (1, 0, 0) direction. there are two inequivalent Cu1+ sites. In the first Cu1+ site, Cu1+ is bonded in a trigonal planar geometry to three P3- atoms. All Cu–P bond lengths are 2.20 Å. In the second Cu1+ site, Cu1+ is bonded to four P3- atoms to form CuP4 tetrahedra that share corners with two equivalent CuP4 tetrahedra and corners with seven GeP4 tetrahedra. There are three shorter (2.23 Å) and one longer (2.29 Å) Cu–P bond lengths. There are four inequivalent Ge4+ sites. In the first Ge4+ site, Ge4+ is bonded in a trigonal non-coplanar geometry to three P3- atoms. There are two shorter (2.32 Å) and one longer (2.33 Å) Ge–P bond lengths. In the second Ge4+ site, Ge4+ is bonded to four P3- atoms to form GeP4 tetrahedra that share corners with two equivalent CuP4 tetrahedra and corners with seven GeP4 tetrahedra. There are a spread of Ge–P bond distances ranging from 2.33–2.43 Å. In the third Ge4+ site, Ge4+ is bonded to four P3- atoms to form GeP4 tetrahedra that share corners with four equivalent CuP4 tetrahedra and corners with five GeP4 tetrahedra. There are a spread of Ge–P bond distances ranging from 2.32–2.38 Å. In the fourth Ge4+ site, Ge4+ is bonded to four P3- atoms to form GeP4 tetrahedra that share a cornercorner with one CuP4 tetrahedra and corners with eight GeP4 tetrahedra. There are a spread of Ge–P bond distances ranging from 2.35–2.41 Å. There are six inequivalent P3- sites. In the first P3- site, P3- is bonded to two Cu1+ and two equivalent Ge4+ atoms to form corner-sharing PCu2Ge2 tetrahedra. In the second P3- site, P3- is bonded to two equivalent Cu1+ and two Ge4+ atoms to form corner-sharing PCu2Ge2 tetrahedra. In the third P3- site, P3- is bonded to two equivalent Cu1+ and two Ge4+ atoms to form corner-sharing PCu2Ge2 tetrahedra. In the fourth P3- site, P3- is bonded in a trigonal non-coplanar geometry to three Ge4+ atoms. In the fifth P3- site, P3- is bonded to one Cu1+ and three Ge4+ atoms to form corner-sharing PCuGe3 tetrahedra. In the sixth P3- site, P3- is bonded in a trigonal non-coplanar geometry to three Ge4+ atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-20. Materials Data on CuGe2P3 by Materials Project. https://doi.org/10.17188/1282376

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗