Materials Data on Na2CeO3 by Materials Project

Abstract

Na2CeO3 is High Pressure (4-7GPa) Tellurium-derived structured and crystallizes in the monoclinic C2/c space group. The structure is three-dimensional. there are seven inequivalent Na1+ sites. In the first Na1+ site, Na1+ is bonded to six O2- atoms to form NaO6 octahedra that share corners with three CeO6 octahedra, edges with four CeO6 octahedra, and edges with five NaO6 octahedra. The corner-sharing octahedra tilt angles range from 10–21°. There are a spread of Na–O bond distances ranging from 2.35–2.51 Å. In the second Na1+ site, Na1+ is bonded in a 6-coordinate geometry to six O2- atoms. There are a spread of Na–O bond distances ranging from 2.28–2.68 Å. In the third Na1+ site, Na1+ is bonded in a 6-coordinate geometry to six O2- atoms. There are a spread of Na–O bond distances ranging from 2.44–2.52 Å. In the fourth Na1+ site, Na1+ is bonded to six O2- atoms to form distorted NaO6 octahedra that share corners with five CeO6 octahedra, edges with four CeO6 octahedra, and edges with five NaO6 octahedra. The corner-sharing octahedra tilt angles range from 3–11°. There are a spread of Na–O bond distances ranging from 2.33–2.57 Å. In the fifth Na1+ site, Na1+ is bonded to six O2- atoms to form distorted NaO6 octahedra that share corners with four CeO6 octahedra, edges with four NaO6 octahedra, and edges with four CeO6 octahedra. The corner-sharing octahedra tilt angles range from 10–14°. There are a spread of Na–O bond distances ranging from 2.27–2.52 Å. In the sixth Na1+ site, Na1+ is bonded in a 6-coordinate geometry to six O2- atoms. There are a spread of Na–O bond distances ranging from 2.37–2.62 Å. In the seventh Na1+ site, Na1+ is bonded to six O2- atoms to form NaO6 octahedra that share corners with four CeO6 octahedra, edges with four NaO6 octahedra, and edges with four CeO6 octahedra. The corner-sharing octahedra tilt angles range from 11–15°. There are a spread of Na–O bond distances ranging from 2.36–2.54 Å. There are four inequivalent Ce4+ sites. In the first Ce4+ site, Ce4+ is bonded to six O2- atoms to form distorted CeO6 octahedra that share corners with five NaO6 octahedra, edges with four NaO6 octahedra, and edges with four CeO6 octahedra. The corner-sharing octahedra tilt angles range from 3–15°. There are a spread of Ce–O bond distances ranging from 2.21–2.38 Å. In the second Ce4+ site, Ce4+ is bonded to six O2- atoms to form distorted CeO6 octahedra that share corners with four NaO6 octahedra, edges with three CeO6 octahedra, and edges with four NaO6 octahedra. The corner-sharing octahedra tilt angles range from 11–21°. There are a spread of Ce–O bond distances ranging from 2.08–2.47 Å. In the third Ce4+ site, Ce4+ is bonded to six O2- atoms to form CeO6 octahedra that share corners with six NaO6 octahedra, edges with three CeO6 octahedra, and edges with six NaO6 octahedra. The corner-sharing octahedra tilt angles range from 8–11°. There are a spread of Ce–O bond distances ranging from 2.23–2.30 Å. In the fourth Ce4+ site, Ce4+ is bonded to six O2- atoms to form CeO6 octahedra that share corners with four NaO6 octahedra, edges with three CeO6 octahedra, and edges with six NaO6 octahedra. The corner-sharing octahedral tilt angles are 11°. There are a spread of Ce–O bond distances ranging from 2.26–2.30 Å. There are nine inequivalent O2- sites. In the first O2- site, O2- is bonded in a 6-coordinate geometry to five Na1+ and one Ce4+ atom. In the second O2- site, O2- is bonded in a 6-coordinate geometry to four Na1+ and two Ce4+ atoms. In the third O2- site, O2- is bonded to three Na1+ and three Ce4+ atoms to form a mixture of edge and corner-sharing ONa3Ce3 octahedra. The corner-sharing octahedra tilt angles range from 0–15°. In the fourth O2- site, O2- is bonded to four Na1+ and two Ce4+ atoms to form distorted ONa4Ce2 octahedra that share corners with four ONa3Ce3 octahedra and edges with eight ONa4Ce2 octahedra. The corner-sharing octahedra tilt angles range from 7–9°. In the fifth O2- site, O2- is bonded to four Na1+ and two Ce4+ atoms to form distorted ONa4Ce2 octahedra that share corners with three ONa4Ce2 octahedra and edges with eight ONa3Ce3 octahedra. The corner-sharing octahedra tilt angles range from 3–12°. In the sixth O2- site, O2- is bonded to four Na1+ and two Ce4+ atoms to form a mixture of distorted edge and corner-sharing ONa4Ce2 octahedra. The corner-sharing octahedra tilt angles range from 6–12°. In the seventh O2- site, O2- is bonded to four Na1+ and two Ce4+ atoms to form distorted ONa4Ce2 octahedra that share corners with three ONa4Ce2 octahedra and edges with nine ONa3Ce3 octahedra. The corner-sharing octahedra tilt angles range from 6–9°. In the eighth O2- site, O2- is bonded in a 6-coordinate geometry to four Na1+ and two Ce4+ atoms. In the ninth O2- site, O2- is bonded to four Na1+ and two Ce4+ atoms to form a mixture of edge and corner-sharing ONa4Ce2 octahedra. The corner-sharing octahedra tilt angles range from 0–15°.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-02. Materials Data on Na2CeO3 by Materials Project. https://doi.org/10.17188/1282392

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗