Materials Data on Cr4Cu3Se8 by Materials Project

Abstract

Cr4Cu3Se8 crystallizes in the orthorhombic Imm2 space group. The structure is three-dimensional. there are two inequivalent Cr3+ sites. In the first Cr3+ site, Cr3+ is bonded to six Se2- atoms to form CrSe6 octahedra that share corners with nine CuSe4 tetrahedra and edges with two equivalent CrSe6 octahedra. There are a spread of Cr–Se bond distances ranging from 2.52–2.57 Å. In the second Cr3+ site, Cr3+ is bonded in a 6-coordinate geometry to six Se2- atoms. There are a spread of Cr–Se bond distances ranging from 2.51–2.75 Å. There are three inequivalent Cu+1.33+ sites. In the first Cu+1.33+ site, Cu+1.33+ is bonded to four Se2- atoms to form CuSe4 tetrahedra that share corners with six equivalent CrSe6 octahedra and an edgeedge with one CuSe4 tetrahedra. The corner-sharing octahedra tilt angles range from 57–60°. There are two shorter (2.39 Å) and two longer (2.52 Å) Cu–Se bond lengths. In the second Cu+1.33+ site, Cu+1.33+ is bonded to four Se2- atoms to form distorted CuSe4 tetrahedra that share corners with six equivalent CrSe6 octahedra, corners with two equivalent CuSe4 tetrahedra, and an edgeedge with one CuSe4 tetrahedra. The corner-sharing octahedra tilt angles range from 46–55°. There are two shorter (2.35 Å) and two longer (2.46 Å) Cu–Se bond lengths. In the third Cu+1.33+ site, Cu+1.33+ is bonded to four Se2- atoms to form CuSe4 tetrahedra that share corners with six equivalent CrSe6 octahedra and corners with two equivalent CuSe4 tetrahedra. The corner-sharing octahedra tilt angles range from 53–56°. There are two shorter (2.41 Å) and two longer (2.44 Å) Cu–Se bond lengths. There are four inequivalent Se2- sites. In the first Se2- site, Se2- is bonded to three Cr3+ and one Cu+1.33+ atom to form a mixture of distorted edge and corner-sharing SeCr3Cu trigonal pyramids. In the second Se2- site, Se2- is bonded in a 5-coordinate geometry to three Cr3+ and two Cu+1.33+ atoms. In the third Se2- site, Se2- is bonded to three Cr3+ and one Cu+1.33+ atom to form a mixture of distorted edge and corner-sharing SeCr3Cu trigonal pyramids. In the fourth Se2- site, Se2- is bonded in a 5-coordinate geometry to three Cr3+ and two Cu+1.33+ atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-02. Materials Data on Cr4Cu3Se8 by Materials Project. https://doi.org/10.17188/1282451

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗