Materials Data on NdZr9O20 by Materials Project

Abstract

NdZr9O20 crystallizes in the triclinic P1 space group. The structure is three-dimensional. Nd is bonded in a body-centered cubic geometry to eight O atoms. There are a spread of Nd–O bond distances ranging from 2.32–2.53 Å. There are nine inequivalent Zr sites. In the first Zr site, Zr is bonded in a distorted body-centered cubic geometry to eight O atoms. There are a spread of Zr–O bond distances ranging from 2.08–2.53 Å. In the second Zr site, Zr is bonded in a distorted body-centered cubic geometry to eight O atoms. There are a spread of Zr–O bond distances ranging from 2.08–2.52 Å. In the third Zr site, Zr is bonded in a 8-coordinate geometry to eight O atoms. There are a spread of Zr–O bond distances ranging from 2.07–2.62 Å. In the fourth Zr site, Zr is bonded in a distorted body-centered cubic geometry to eight O atoms. There are a spread of Zr–O bond distances ranging from 2.08–2.49 Å. In the fifth Zr site, Zr is bonded in a distorted body-centered cubic geometry to eight O atoms. There are a spread of Zr–O bond distances ranging from 2.08–2.51 Å. In the sixth Zr site, Zr is bonded in a distorted body-centered cubic geometry to eight O atoms. There are a spread of Zr–O bond distances ranging from 2.11–2.52 Å. In the seventh Zr site, Zr is bonded in a distorted body-centered cubic geometry to eight O atoms. There are a spread of Zr–O bond distances ranging from 2.11–2.53 Å. In the eighth Zr site, Zr is bonded in a distorted body-centered cubic geometry to eight O atoms. There are a spread of Zr–O bond distances ranging from 2.09–2.58 Å. In the ninth Zr site, Zr is bonded in a distorted body-centered cubic geometry to eight O atoms. There are a spread of Zr–O bond distances ranging from 2.11–2.50 Å. There are twenty inequivalent O sites. In the first O site, O is bonded to four Zr atoms to form a mixture of distorted corner and edge-sharing OZr4 tetrahedra. In the second O site, O is bonded to four Zr atoms to form a mixture of distorted corner and edge-sharing OZr4 tetrahedra. In the third O site, O is bonded in a 4-coordinate geometry to four Zr atoms. In the fourth O site, O is bonded to four Zr atoms to form a mixture of distorted corner and edge-sharing OZr4 tetrahedra. In the fifth O site, O is bonded to four Zr atoms to form a mixture of distorted corner and edge-sharing OZr4 tetrahedra. In the sixth O site, O is bonded in a 4-coordinate geometry to four Zr atoms. In the seventh O site, O is bonded to one Nd and three Zr atoms to form a mixture of distorted corner and edge-sharing ONdZr3 tetrahedra. In the eighth O site, O is bonded to four Zr atoms to form distorted OZr4 tetrahedra that share corners with sixteen OZr4 tetrahedra and edges with four ONdZr3 tetrahedra. In the ninth O site, O is bonded to four Zr atoms to form a mixture of distorted corner and edge-sharing OZr4 tetrahedra. In the tenth O site, O is bonded to four Zr atoms to form a mixture of distorted corner and edge-sharing OZr4 tetrahedra. In the eleventh O site, O is bonded to one Nd and three Zr atoms to form a mixture of distorted corner and edge-sharing ONdZr3 tetrahedra. In the twelfth O site, O is bonded to one Nd and three Zr atoms to form ONdZr3 tetrahedra that share corners with fourteen OZr4 tetrahedra and edges with six ONdZr3 tetrahedra. In the thirteenth O site, O is bonded to one Nd and three Zr atoms to form a mixture of corner and edge-sharing ONdZr3 tetrahedra. In the fourteenth O site, O is bonded to one Nd and three Zr atoms to form a mixture of distorted corner and edge-sharing ONdZr3 tetrahedra. In the fifteenth O site, O is bonded to four Zr atoms to form a mixture of distorted corner and edge-sharing OZr4 tetrahedra. In the sixteenth O site, O is bonded to one Nd and three Zr atoms to form ONdZr3 tetrahedra that share corners with fifteen OZr4 tetrahedra and edges with five ONdZr3 tetrahedra. In the seventeenth O site, O is bonded to four Zr atoms to form distorted OZr4 tetrahedra that share corners with fifteen OZr4 tetrahedra and edges with five ONdZr3 tetrahedra. In the eighteenth O site, O is bonded to four Zr atoms to form a mixture of distorted corner and edge-sharing OZr4 tetrahedra. In the nineteenth O site, O is bonded to one Nd and three Zr atoms to form a mixture of corner and edge-sharing ONdZr3 tetrahedra. In the twentieth O site, O is bonded to one Nd and three Zr atoms to form a mixture of distorted corner and edge-sharing ONdZr3 tetrahedra.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-02. Materials Data on NdZr9O20 by Materials Project. https://doi.org/10.17188/1282496

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗