Materials Data on InCuSe2 by Materials Project

Abstract

CuInSe2 is Caswellsilverite-like structured and crystallizes in the triclinic P1 space group. The structure is three-dimensional. there are two inequivalent Cu1+ sites. In the first Cu1+ site, Cu1+ is bonded to six Se2- atoms to form CuSe6 octahedra that share corners with two equivalent InSe6 octahedra, corners with four equivalent CuSe6 octahedra, edges with four equivalent CuSe6 octahedra, and edges with eight InSe6 octahedra. The corner-sharing octahedra tilt angles range from 0–6°. There are a spread of Cu–Se bond distances ranging from 2.58–2.81 Å. In the second Cu1+ site, Cu1+ is bonded to six Se2- atoms to form CuSe6 octahedra that share corners with two equivalent InSe6 octahedra, corners with four equivalent CuSe6 octahedra, edges with four equivalent CuSe6 octahedra, and edges with eight InSe6 octahedra. The corner-sharing octahedra tilt angles range from 1–6°. There are a spread of Cu–Se bond distances ranging from 2.58–2.83 Å. There are two inequivalent In3+ sites. In the first In3+ site, In3+ is bonded to six Se2- atoms to form InSe6 octahedra that share corners with two equivalent CuSe6 octahedra, corners with four equivalent InSe6 octahedra, edges with four equivalent InSe6 octahedra, and edges with eight CuSe6 octahedra. The corner-sharing octahedra tilt angles range from 0–6°. There are a spread of In–Se bond distances ranging from 2.78–2.86 Å. In the second In3+ site, In3+ is bonded to six Se2- atoms to form InSe6 octahedra that share corners with two equivalent CuSe6 octahedra, corners with four equivalent InSe6 octahedra, edges with four equivalent InSe6 octahedra, and edges with eight CuSe6 octahedra. The corner-sharing octahedra tilt angles range from 1–6°. There are a spread of In–Se bond distances ranging from 2.78–2.86 Å. There are four inequivalent Se2- sites. In the first Se2- site, Se2- is bonded to three Cu1+ and three In3+ atoms to form a mixture of corner and edge-sharing SeIn3Cu3 octahedra. The corner-sharing octahedra tilt angles range from 1–6°. In the second Se2- site, Se2- is bonded to three Cu1+ and three In3+ atoms to form a mixture of corner and edge-sharing SeIn3Cu3 octahedra. The corner-sharing octahedra tilt angles range from 0–6°. In the third Se2- site, Se2- is bonded to three Cu1+ and three In3+ atoms to form a mixture of corner and edge-sharing SeIn3Cu3 octahedra. The corner-sharing octahedra tilt angles range from 1–5°. In the fourth Se2- site, Se2- is bonded to three Cu1+ and three In3+ atoms to form a mixture of corner and edge-sharing SeIn3Cu3 octahedra. The corner-sharing octahedra tilt angles range from 0–5°.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-23. Materials Data on InCuSe2 by Materials Project. https://doi.org/10.17188/1283161

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗