Materials Data on Ta14(CuS8)3 by Materials Project

Abstract

Ta14(CuS8)3 crystallizes in the triclinic P1 space group. The structure is three-dimensional. there are fourteen inequivalent Ta+3.21+ sites. In the first Ta+3.21+ site, Ta+3.21+ is bonded to six S2- atoms to form distorted TaS6 pentagonal pyramids that share corners with two TaS6 octahedra, a cornercorner with one CuS4 trigonal pyramid, and edges with six TaS6 pentagonal pyramids. The corner-sharing octahedra tilt angles range from 43–48°. There are a spread of Ta–S bond distances ranging from 2.45–2.51 Å. In the second Ta+3.21+ site, Ta+3.21+ is bonded to six S2- atoms to form distorted TaS6 pentagonal pyramids that share corners with three TaS6 octahedra, a cornercorner with one CuS4 trigonal pyramid, and edges with six TaS6 pentagonal pyramids. The corner-sharing octahedra tilt angles range from 47–49°. There are a spread of Ta–S bond distances ranging from 2.47–2.51 Å. In the third Ta+3.21+ site, Ta+3.21+ is bonded to six S2- atoms to form distorted TaS6 pentagonal pyramids that share corners with two TaS6 octahedra, a cornercorner with one CuS4 trigonal pyramid, and edges with six TaS6 pentagonal pyramids. The corner-sharing octahedra tilt angles range from 45–46°. There are a spread of Ta–S bond distances ranging from 2.46–2.51 Å. In the fourth Ta+3.21+ site, Ta+3.21+ is bonded to six S2- atoms to form a mixture of corner, edge, and face-sharing TaS6 octahedra. There are a spread of Ta–S bond distances ranging from 2.45–2.58 Å. In the fifth Ta+3.21+ site, Ta+3.21+ is bonded to six S2- atoms to form distorted TaS6 pentagonal pyramids that share a cornercorner with one TaS6 octahedra, a cornercorner with one CuS4 trigonal pyramid, edges with six TaS6 pentagonal pyramids, and a faceface with one TaS6 octahedra. The corner-sharing octahedral tilt angles are 51°. There are a spread of Ta–S bond distances ranging from 2.45–2.53 Å. In the sixth Ta+3.21+ site, Ta+3.21+ is bonded to six S2- atoms to form distorted TaS6 pentagonal pyramids that share corners with three TaS6 octahedra, edges with six TaS6 pentagonal pyramids, and a faceface with one CuS4 trigonal pyramid. The corner-sharing octahedra tilt angles range from 40–43°. There are a spread of Ta–S bond distances ranging from 2.46–2.56 Å. In the seventh Ta+3.21+ site, Ta+3.21+ is bonded to six S2- atoms to form a mixture of distorted corner, edge, and face-sharing TaS6 pentagonal pyramids. The corner-sharing octahedral tilt angles are 52°. There are a spread of Ta–S bond distances ranging from 2.45–2.53 Å. In the eighth Ta+3.21+ site, Ta+3.21+ is bonded to six S2- atoms to form distorted TaS6 pentagonal pyramids that share a cornercorner with one TaS6 octahedra, corners with two equivalent CuS4 trigonal pyramids, edges with six TaS6 pentagonal pyramids, and a faceface with one TaS6 octahedra. The corner-sharing octahedral tilt angles are 52°. There are a spread of Ta–S bond distances ranging from 2.46–2.52 Å. In the ninth Ta+3.21+ site, Ta+3.21+ is bonded to six S2- atoms to form a mixture of distorted corner and edge-sharing TaS6 pentagonal pyramids. The corner-sharing octahedra tilt angles range from 40–43°. There are a spread of Ta–S bond distances ranging from 2.46–2.56 Å. In the tenth Ta+3.21+ site, Ta+3.21+ is bonded to six S2- atoms to form distorted TaS6 pentagonal pyramids that share a cornercorner with one TaS6 octahedra, a cornercorner with one CuS4 trigonal pyramid, edges with six TaS6 pentagonal pyramids, and a faceface with one TaS6 octahedra. The corner-sharing octahedral tilt angles are 51°. There are a spread of Ta–S bond distances ranging from 2.45–2.52 Å. In the eleventh Ta+3.21+ site, Ta+3.21+ is bonded to six S2- atoms to form a mixture of corner, edge, and face-sharing TaS6 octahedra. There are a spread of Ta–S bond distances ranging from 2.44–2.59 Å. In the twelfth Ta+3.21+ site, Ta+3.21+ is bonded to six S2- atoms to form a mixture of distorted corner and edge-sharing TaS6 pentagonal pyramids. The corner-sharing octahedral tilt angles are 45°. There are a spread of Ta–S bond distances ranging from 2.45–2.55 Å. In the thirteenth Ta+3.21+ site, Ta+3.21+ is bonded to six S2- atoms to form distorted TaS6 pentagonal pyramids that share corners with three TaS6 octahedra, a cornercorner with one CuS4 trigonal pyramid, and edges with six TaS6 pentagonal pyramids. The corner-sharing octahedra tilt angles range from 47–49°. There are a spread of Ta–S bond distances ranging from 2.47–2.52 Å. In the fourteenth Ta+3.21+ site, Ta+3.21+ is bonded to six S2- atoms to form distorted TaS6 pentagonal pyramids that share corners with two TaS6 octahedra, a cornercorner with one CuS4 trigonal pyramid, and edges with six TaS6 pentagonal pyramids. The corner-sharing octahedra tilt angles range from 42–48°. There are a spread of Ta–S bond distances ranging from 2.46–2.51 Å. There are three inequivalent Cu1+ sites. In the first Cu1+ site, Cu1+ is bonded to four S2- atoms to form distorted CuS4 trigonal pyramids that share corners with nine TaS6 pentagonal pyramids and a faceface with one TaS6 pentagonal pyramid. There are a spread of Cu–S bond distances ranging from 2.23–2.34 Å. In the second Cu1+ site, Cu1+ is bonded in a rectangular see-saw-like geometry to four S2- atoms. There are a spread of Cu–S bond distances ranging from 2.22–2.34 Å. In the third Cu1+ site, Cu1+ is bonded in a distorted rectangular see-saw-like geometry to four S2- atoms. There are a spread of Cu–S bond distances ranging from 2.22–2.33 Å. There are twenty-four inequivalent S2- sites. In the first S2- site, S2- is bonded in a 5-coordinate geometry to three Ta+3.21+ and two Cu1+ atoms. In the second S2- site, S2- is bonded in a 3-coordinate geometry to three Ta+3.21+ atoms. In the third S2- site, S2- is bonded in a distorted rectangular see-saw-like geometry to three Ta+3.21+ and one Cu1+ atom. In the fourth S2- site, S2- is bonded in a distorted rectangular see-saw-like geometry to three Ta+3.21+ and one Cu1+ atom. In the fifth S2- site, S2- is bonded to four Ta+3.21+ atoms to form a mixture of distorted corner and edge-sharing STa4 trigonal pyramids. In the sixth S2- site, S2- is bonded to four Ta+3.21+ atoms to form a mixture of distorted corner and edge-sharing STa4 trigonal pyramids. In the seventh S2- site, S2- is bonded to four Ta+3.21+ atoms to form distorted corner-sharing STa4 trigonal pyramids. In the eighth S2- site, S2- is bonded in a 3-coordinate geometry to three Ta+3.21+ atoms. In the ninth S2- site, S2- is bonded in a rectangular see-saw-like geometry to three Ta+3.21+ and one Cu1+ atom. In the tenth S2- site, S2- is bonded in a distorted rectangular see-saw-like geometry to three Ta+3.21+ and one Cu1+ atom. In the eleventh S2- site, S2- is bonded in a distorted rectangular see-saw-like geometry to four Ta+3.21+ atoms. In the twelfth S2- site, S2- is bonded in a distorted pentagonal planar geometry to five Ta+3.21+ atoms. In the thirteenth S2- site, S2- is bonded in a distorted pentagonal planar geometry to five Ta+3.21+ atoms. In the fourteenth S2- site, S2- is bonded in a rectangular see-saw-like geometry to four Ta+3.21+ atoms. In the fifteenth S2- site, S2- is bonded in a distorted rectangular see-saw-like geometry to three Ta+3.21+ and one Cu1+ atom. In the sixteenth S2- site, S2- is bonded in a rectangular see-saw-like geometry to three Ta+3.21+ and one Cu1+ atom. In the seventeenth S2- site, S2- is bonded in a distorted rectangular see-saw-like geometry to three Ta+3.21+ and one Cu1+ atom. In the eighteenth S2- site, S2- is bonded to four Ta+3.21+ atoms to form distorted corner-sharing STa4 trigonal pyramids. In the nineteenth S2- site, S2- is bonded in a distorted rectangular see-saw-like geometry to four Ta+3.21+ atoms. In the twentieth S2- site, S2- is bonded to four Ta+3.21+ atoms to form distorted corner-sharing STa4 trigonal pyramids. In the twenty-first S2- site, S2- is bonded in a rectangular see-saw-like geometry to three Ta+3.21+ and one Cu1+ atom. In the twenty-second S2- site, S2- is bonded in a distorted rectangular see-saw-like geometry to three Ta+3.21+ and one Cu1+ atom. In the twenty-third S2- site, S2- is bonded in a 3-coordinate geometry to three Ta+3.21+ atoms. In the twenty-fourth S2- site, S2- is bonded in a distorted rectangular see-saw-like geometry to three Ta+3.21+ and one Cu1+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-30. Materials Data on Ta14(CuS8)3 by Materials Project. https://doi.org/10.17188/1283182

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗