Materials Data on Cu2Bi8Pb2S15 by Materials Project

Abstract

Cu2Pb2Bi8S15 crystallizes in the orthorhombic Pnma space group. The structure is three-dimensional. there are two inequivalent Cu1+ sites. In the first Cu1+ site, Cu1+ is bonded to four S2- atoms to form corner-sharing CuS4 tetrahedra. There are a spread of Cu–S bond distances ranging from 2.32–2.43 Å. In the second Cu1+ site, Cu1+ is bonded to four S2- atoms to form corner-sharing CuS4 tetrahedra. There are a spread of Cu–S bond distances ranging from 2.32–2.43 Å. There are two inequivalent Pb2+ sites. In the first Pb2+ site, Pb2+ is bonded in a 8-coordinate geometry to eight S2- atoms. There are a spread of Pb–S bond distances ranging from 2.98–3.55 Å. In the second Pb2+ site, Pb2+ is bonded in a 7-coordinate geometry to seven S2- atoms. There are a spread of Pb–S bond distances ranging from 2.97–3.19 Å. There are eight inequivalent Bi3+ sites. In the first Bi3+ site, Bi3+ is bonded in a 7-coordinate geometry to seven S2- atoms. There are a spread of Bi–S bond distances ranging from 2.70–3.44 Å. In the second Bi3+ site, Bi3+ is bonded in a 6-coordinate geometry to six S2- atoms. There are a spread of Bi–S bond distances ranging from 2.71–3.08 Å. In the third Bi3+ site, Bi3+ is bonded in a 7-coordinate geometry to seven S2- atoms. There are a spread of Bi–S bond distances ranging from 2.69–3.46 Å. In the fourth Bi3+ site, Bi3+ is bonded in a 6-coordinate geometry to six S2- atoms. There are a spread of Bi–S bond distances ranging from 2.70–3.08 Å. In the fifth Bi3+ site, Bi3+ is bonded to six S2- atoms to form distorted edge-sharing BiS6 octahedra. There are a spread of Bi–S bond distances ranging from 2.71–3.01 Å. In the sixth Bi3+ site, Bi3+ is bonded in a 5-coordinate geometry to seven S2- atoms. There are a spread of Bi–S bond distances ranging from 2.63–3.47 Å. In the seventh Bi3+ site, Bi3+ is bonded in a 7-coordinate geometry to seven S2- atoms. There are a spread of Bi–S bond distances ranging from 2.63–3.38 Å. In the eighth Bi3+ site, Bi3+ is bonded in a 5-coordinate geometry to five S2- atoms. There are a spread of Bi–S bond distances ranging from 2.63–3.00 Å. There are fifteen inequivalent S2- sites. In the first S2- site, S2- is bonded in a 3-coordinate geometry to two equivalent Cu1+, two equivalent Pb2+, and one Bi3+ atom. In the second S2- site, S2- is bonded to one Cu1+, one Pb2+, and four Bi3+ atoms to form distorted SCuBi4Pb octahedra that share edges with two equivalent SCuBi4Pb octahedra and edges with two equivalent SBi3Pb2 square pyramids. In the third S2- site, S2- is bonded in a 3-coordinate geometry to three Bi3+ atoms. In the fourth S2- site, S2- is bonded to two equivalent Pb2+ and three Bi3+ atoms to form distorted SBi3Pb2 square pyramids that share edges with two equivalent SCuBi4Pb octahedra and edges with two equivalent SBi3Pb2 square pyramids. In the fifth S2- site, S2- is bonded in a 3-coordinate geometry to two equivalent Cu1+, two equivalent Pb2+, and two Bi3+ atoms. In the sixth S2- site, S2- is bonded in a 4-coordinate geometry to four Bi3+ atoms. In the seventh S2- site, S2- is bonded in a 3-coordinate geometry to one Pb2+ and three Bi3+ atoms. In the eighth S2- site, S2- is bonded in a 5-coordinate geometry to five Bi3+ atoms. In the ninth S2- site, S2- is bonded in a 5-coordinate geometry to two equivalent Pb2+ and three Bi3+ atoms. In the tenth S2- site, S2- is bonded in a 4-coordinate geometry to one Cu1+ and three Bi3+ atoms. In the eleventh S2- site, S2- is bonded in a 5-coordinate geometry to two equivalent Pb2+ and three Bi3+ atoms. In the twelfth S2- site, S2- is bonded in a 4-coordinate geometry to one Cu1+ and five Bi3+ atoms. In the thirteenth S2- site, S2- is bonded to two equivalent Pb2+ and three Bi3+ atoms to form distorted SBi3Pb2 square pyramids that share edges with two equivalent SCuBi4Pb octahedra and edges with two equivalent SBi3Pb2 square pyramids. In the fourteenth S2- site, S2- is bonded to five Bi3+ atoms to form distorted edge-sharing SBi5 square pyramids. In the fifteenth S2- site, S2- is bonded to one Cu1+, one Pb2+, and four Bi3+ atoms to form distorted SCuBi4Pb octahedra that share edges with two equivalent SCuBi4Pb octahedra and edges with two equivalent SBi3Pb2 square pyramids.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on Cu2Bi8Pb2S15 by Materials Project. https://doi.org/10.17188/1283643

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗