Materials Data on Ce6Si4S17 by Materials Project

Abstract

Ce6Si4S17 crystallizes in the triclinic P-1 space group. The structure is three-dimensional. there are six inequivalent Ce3+ sites. In the first Ce3+ site, Ce3+ is bonded in a 8-coordinate geometry to eight S2- atoms. There are a spread of Ce–S bond distances ranging from 2.89–3.27 Å. In the second Ce3+ site, Ce3+ is bonded in a 9-coordinate geometry to nine S2- atoms. There are a spread of Ce–S bond distances ranging from 2.77–3.43 Å. In the third Ce3+ site, Ce3+ is bonded in a 8-coordinate geometry to eight S2- atoms. There are a spread of Ce–S bond distances ranging from 2.90–3.17 Å. In the fourth Ce3+ site, Ce3+ is bonded to seven S2- atoms to form distorted CeS7 pentagonal bipyramids that share corners with two SiS4 tetrahedra and edges with two SiS4 tetrahedra. There are a spread of Ce–S bond distances ranging from 2.86–3.05 Å. In the fifth Ce3+ site, Ce3+ is bonded in a 9-coordinate geometry to nine S2- atoms. There are a spread of Ce–S bond distances ranging from 2.89–3.31 Å. In the sixth Ce3+ site, Ce3+ is bonded in a 8-coordinate geometry to eight S2- atoms. There are a spread of Ce–S bond distances ranging from 2.88–3.25 Å. There are four inequivalent Si4+ sites. In the first Si4+ site, Si4+ is bonded to four S2- atoms to form SiS4 tetrahedra that share a cornercorner with one CeS7 pentagonal bipyramid and an edgeedge with one CeS7 pentagonal bipyramid. There are a spread of Si–S bond distances ranging from 2.10–2.16 Å. In the second Si4+ site, Si4+ is bonded to four S2- atoms to form SiS4 tetrahedra that share an edgeedge with one CeS7 pentagonal bipyramid. There are a spread of Si–S bond distances ranging from 2.12–2.15 Å. In the third Si4+ site, Si4+ is bonded to four S2- atoms to form SiS4 tetrahedra that share a cornercorner with one CeS7 pentagonal bipyramid. There are a spread of Si–S bond distances ranging from 2.10–2.15 Å. In the fourth Si4+ site, Si4+ is bonded in a tetrahedral geometry to four S2- atoms. There are a spread of Si–S bond distances ranging from 2.10–2.15 Å. There are seventeen inequivalent S2- sites. In the first S2- site, S2- is bonded to three Ce3+ and one Si4+ atom to form distorted SCe3Si trigonal pyramids that share a cornercorner with one SCe4 tetrahedra and corners with two SCe3Si trigonal pyramids. In the second S2- site, S2- is bonded in a 4-coordinate geometry to three Ce3+ and one Si4+ atom. In the third S2- site, S2- is bonded in a 1-coordinate geometry to three Ce3+ and one Si4+ atom. In the fourth S2- site, S2- is bonded to four Ce3+ atoms to form a mixture of corner and edge-sharing SCe4 tetrahedra. In the fifth S2- site, S2- is bonded in a 3-coordinate geometry to two Ce3+ and one Si4+ atom. In the sixth S2- site, S2- is bonded in a 4-coordinate geometry to three Ce3+ and one Si4+ atom. In the seventh S2- site, S2- is bonded in a distorted rectangular see-saw-like geometry to three Ce3+ and one Si4+ atom. In the eighth S2- site, S2- is bonded in a 3-coordinate geometry to two Ce3+ and one Si4+ atom. In the ninth S2- site, S2- is bonded in a 4-coordinate geometry to three Ce3+ and one Si4+ atom. In the tenth S2- site, S2- is bonded in a distorted rectangular see-saw-like geometry to three Ce3+ and one Si4+ atom. In the eleventh S2- site, S2- is bonded in a distorted T-shaped geometry to two Ce3+ and one Si4+ atom. In the twelfth S2- site, S2- is bonded to three Ce3+ and one Si4+ atom to form distorted SCe3Si trigonal pyramids that share corners with two SCe3Si trigonal pyramids and an edgeedge with one SCe4 tetrahedra. In the thirteenth S2- site, S2- is bonded in a 4-coordinate geometry to three Ce3+ and one Si4+ atom. In the fourteenth S2- site, S2- is bonded in a 3-coordinate geometry to two Ce3+ and one Si4+ atom. In the fifteenth S2- site, S2- is bonded in a 4-coordinate geometry to three Ce3+ and one Si4+ atom. In the sixteenth S2- site, S2- is bonded in a 1-coordinate geometry to four Ce3+ and one Si4+ atom. In the seventeenth S2- site, S2- is bonded to three Ce3+ and one Si4+ atom to form distorted SCe3Si trigonal pyramids that share corners with two SCe3Si trigonal pyramids and an edgeedge with one SCe4 tetrahedra.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on Ce6Si4S17 by Materials Project. https://doi.org/10.17188/1283712

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗