Materials Data on Sc12I25 by Materials Project

Abstract

Sc12I25 crystallizes in the triclinic P-1 space group. The structure is two-dimensional and consists of one Sc12I25 sheet oriented in the (1, -1, 1) direction. there are twelve inequivalent Sc+2.08+ sites. In the first Sc+2.08+ site, Sc+2.08+ is bonded to six I1- atoms to form edge-sharing ScI6 octahedra. There are a spread of Sc–I bond distances ranging from 2.88–2.98 Å. In the second Sc+2.08+ site, Sc+2.08+ is bonded to six I1- atoms to form edge-sharing ScI6 octahedra. There are a spread of Sc–I bond distances ranging from 2.92–3.00 Å. In the third Sc+2.08+ site, Sc+2.08+ is bonded to six I1- atoms to form edge-sharing ScI6 octahedra. There are a spread of Sc–I bond distances ranging from 2.88–2.97 Å. In the fourth Sc+2.08+ site, Sc+2.08+ is bonded to six I1- atoms to form edge-sharing ScI6 octahedra. There are a spread of Sc–I bond distances ranging from 2.94–2.98 Å. In the fifth Sc+2.08+ site, Sc+2.08+ is bonded to six I1- atoms to form edge-sharing ScI6 octahedra. There are a spread of Sc–I bond distances ranging from 2.93–2.96 Å. In the sixth Sc+2.08+ site, Sc+2.08+ is bonded to six I1- atoms to form edge-sharing ScI6 octahedra. There are a spread of Sc–I bond distances ranging from 2.87–2.98 Å. In the seventh Sc+2.08+ site, Sc+2.08+ is bonded to six I1- atoms to form edge-sharing ScI6 octahedra. There are a spread of Sc–I bond distances ranging from 2.94–2.97 Å. In the eighth Sc+2.08+ site, Sc+2.08+ is bonded to six I1- atoms to form edge-sharing ScI6 octahedra. There are a spread of Sc–I bond distances ranging from 2.90–3.00 Å. In the ninth Sc+2.08+ site, Sc+2.08+ is bonded to six I1- atoms to form edge-sharing ScI6 octahedra. There are a spread of Sc–I bond distances ranging from 2.93–2.98 Å. In the tenth Sc+2.08+ site, Sc+2.08+ is bonded to six I1- atoms to form edge-sharing ScI6 octahedra. There are a spread of Sc–I bond distances ranging from 2.91–2.99 Å. In the eleventh Sc+2.08+ site, Sc+2.08+ is bonded to six I1- atoms to form edge-sharing ScI6 octahedra. There are a spread of Sc–I bond distances ranging from 2.95–2.98 Å. In the twelfth Sc+2.08+ site, Sc+2.08+ is bonded to six I1- atoms to form edge-sharing ScI6 octahedra. There are a spread of Sc–I bond distances ranging from 2.92–2.96 Å. There are twenty-five inequivalent I1- sites. In the first I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the second I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the third I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the fourth I1- site, I1- is bonded in an L-shaped geometry to two Sc+2.08+ atoms. In the fifth I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the sixth I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the seventh I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the eighth I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the ninth I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the tenth I1- site, I1- is bonded in an L-shaped geometry to two Sc+2.08+ atoms. In the eleventh I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the twelfth I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the thirteenth I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the fourteenth I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the fifteenth I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the sixteenth I1- site, I1- is bonded in an L-shaped geometry to two Sc+2.08+ atoms. In the seventeenth I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the eighteenth I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the nineteenth I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the twentieth I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the twenty-first I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the twenty-second I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the twenty-third I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the twenty-fourth I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms. In the twenty-fifth I1- site, I1- is bonded in a distorted T-shaped geometry to three Sc+2.08+ atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on Sc12I25 by Materials Project. https://doi.org/10.17188/1284093

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗