Materials Data on Ti4P8S29 by Materials Project

Abstract

Ti4P8S29 crystallizes in the monoclinic Cc space group. The structure is two-dimensional and consists of two Ti4P8S29 sheets oriented in the (0, 1, 0) direction. there are four inequivalent Ti+3.50+ sites. In the first Ti+3.50+ site, Ti+3.50+ is bonded to six S+1.86- atoms to form distorted TiS6 octahedra that share edges with three PS4 tetrahedra. There are a spread of Ti–S bond distances ranging from 2.40–2.55 Å. In the second Ti+3.50+ site, Ti+3.50+ is bonded to six S+1.86- atoms to form TiS6 octahedra that share edges with three PS4 tetrahedra. There are a spread of Ti–S bond distances ranging from 2.41–2.53 Å. In the third Ti+3.50+ site, Ti+3.50+ is bonded to six S+1.86- atoms to form TiS6 octahedra that share edges with three PS4 tetrahedra. There are a spread of Ti–S bond distances ranging from 2.42–2.53 Å. In the fourth Ti+3.50+ site, Ti+3.50+ is bonded to six S+1.86- atoms to form distorted TiS6 octahedra that share edges with three PS4 tetrahedra. There are a spread of Ti–S bond distances ranging from 2.40–2.53 Å. There are eight inequivalent P5+ sites. In the first P5+ site, P5+ is bonded to four S+1.86- atoms to form PS4 tetrahedra that share an edgeedge with one TiS6 octahedra and an edgeedge with one PS4 tetrahedra. There are a spread of P–S bond distances ranging from 2.01–2.15 Å. In the second P5+ site, P5+ is bonded to four S+1.86- atoms to form PS4 tetrahedra that share edges with two TiS6 octahedra. There are three shorter (2.05 Å) and one longer (2.06 Å) P–S bond lengths. In the third P5+ site, P5+ is bonded to four S+1.86- atoms to form PS4 tetrahedra that share an edgeedge with one TiS6 octahedra and an edgeedge with one PS4 tetrahedra. There are a spread of P–S bond distances ranging from 2.01–2.37 Å. In the fourth P5+ site, P5+ is bonded to four S+1.86- atoms to form PS4 tetrahedra that share edges with two TiS6 octahedra. All P–S bond lengths are 2.05 Å. In the fifth P5+ site, P5+ is bonded to four S+1.86- atoms to form PS4 tetrahedra that share edges with two TiS6 octahedra. There are one shorter (2.05 Å) and three longer (2.06 Å) P–S bond lengths. In the sixth P5+ site, P5+ is bonded to four S+1.86- atoms to form PS4 tetrahedra that share an edgeedge with one TiS6 octahedra and an edgeedge with one PS4 tetrahedra. There are a spread of P–S bond distances ranging from 2.00–2.25 Å. In the seventh P5+ site, P5+ is bonded to four S+1.86- atoms to form PS4 tetrahedra that share edges with two TiS6 octahedra. There are three shorter (2.05 Å) and one longer (2.06 Å) P–S bond lengths. In the eighth P5+ site, P5+ is bonded to four S+1.86- atoms to form PS4 tetrahedra that share an edgeedge with one TiS6 octahedra and an edgeedge with one PS4 tetrahedra. There are a spread of P–S bond distances ranging from 2.01–2.14 Å. There are twenty-nine inequivalent S+1.86- sites. In the first S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the second S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the third S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the fourth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the fifth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the sixth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to two P5+ atoms. In the seventh S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the eighth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the ninth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the tenth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the eleventh S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the twelfth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to two P5+ atoms. In the thirteenth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the fourteenth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the fifteenth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the sixteenth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the seventeenth S+1.86- site, S+1.86- is bonded in a 3-coordinate geometry to two P5+ and one S+1.86- atom. The S–S bond length is 1.92 Å. In the eighteenth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the nineteenth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the twentieth S+1.86- site, S+1.86- is bonded in a distorted single-bond geometry to one S+1.86- atom. In the twenty-first S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the twenty-second S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the twenty-third S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the twenty-fourth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to two P5+ atoms. In the twenty-fifth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the twenty-sixth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the twenty-seventh S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the twenty-eighth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom. In the twenty-ninth S+1.86- site, S+1.86- is bonded in an L-shaped geometry to one Ti+3.50+ and one P5+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-29. Materials Data on Ti4P8S29 by Materials Project. https://doi.org/10.17188/1284147

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗