Materials Data on CeZr11O24 by Materials Project

Abstract

CeZr11O24 is Baddeleyite-derived structured and crystallizes in the triclinic P1 space group. The structure is three-dimensional. Ce4+ is bonded to seven O2- atoms to form distorted CeO7 pentagonal bipyramids that share corners with four ZrO7 pentagonal bipyramids and edges with seven ZrO7 pentagonal bipyramids. There are a spread of Ce–O bond distances ranging from 2.17–2.41 Å. There are eleven inequivalent Zr4+ sites. In the first Zr4+ site, Zr4+ is bonded to seven O2- atoms to form distorted ZrO7 pentagonal bipyramids that share a cornercorner with one CeO7 pentagonal bipyramid, corners with three ZrO7 pentagonal bipyramids, and edges with seven ZrO7 pentagonal bipyramids. There are a spread of Zr–O bond distances ranging from 2.08–2.31 Å. In the second Zr4+ site, Zr4+ is bonded to seven O2- atoms to form distorted ZrO7 pentagonal bipyramids that share corners with four ZrO7 pentagonal bipyramids, an edgeedge with one CeO7 pentagonal bipyramid, and edges with six ZrO7 pentagonal bipyramids. There are a spread of Zr–O bond distances ranging from 2.09–2.27 Å. In the third Zr4+ site, Zr4+ is bonded to seven O2- atoms to form a mixture of distorted corner and edge-sharing ZrO7 pentagonal bipyramids. There are a spread of Zr–O bond distances ranging from 2.09–2.32 Å. In the fourth Zr4+ site, Zr4+ is bonded to seven O2- atoms to form distorted ZrO7 pentagonal bipyramids that share corners with four ZrO7 pentagonal bipyramids, an edgeedge with one CeO7 pentagonal bipyramid, and edges with six ZrO7 pentagonal bipyramids. There are a spread of Zr–O bond distances ranging from 2.07–2.32 Å. In the fifth Zr4+ site, Zr4+ is bonded to seven O2- atoms to form distorted ZrO7 pentagonal bipyramids that share corners with four ZrO7 pentagonal bipyramids, edges with two equivalent CeO7 pentagonal bipyramids, and edges with five ZrO7 pentagonal bipyramids. There are a spread of Zr–O bond distances ranging from 2.09–2.32 Å. In the sixth Zr4+ site, Zr4+ is bonded to seven O2- atoms to form distorted ZrO7 pentagonal bipyramids that share corners with four ZrO7 pentagonal bipyramids, an edgeedge with one CeO7 pentagonal bipyramid, and edges with six ZrO7 pentagonal bipyramids. There are a spread of Zr–O bond distances ranging from 2.07–2.32 Å. In the seventh Zr4+ site, Zr4+ is bonded to seven O2- atoms to form a mixture of distorted corner and edge-sharing ZrO7 pentagonal bipyramids. There are a spread of Zr–O bond distances ranging from 2.09–2.30 Å. In the eighth Zr4+ site, Zr4+ is bonded to seven O2- atoms to form distorted ZrO7 pentagonal bipyramids that share a cornercorner with one CeO7 pentagonal bipyramid, corners with three ZrO7 pentagonal bipyramids, an edgeedge with one CeO7 pentagonal bipyramid, and edges with six ZrO7 pentagonal bipyramids. There are a spread of Zr–O bond distances ranging from 2.09–2.33 Å. In the ninth Zr4+ site, Zr4+ is bonded to seven O2- atoms to form a mixture of distorted corner and edge-sharing ZrO7 pentagonal bipyramids. There are a spread of Zr–O bond distances ranging from 2.09–2.30 Å. In the tenth Zr4+ site, Zr4+ is bonded to seven O2- atoms to form distorted ZrO7 pentagonal bipyramids that share a cornercorner with one CeO7 pentagonal bipyramid, corners with three ZrO7 pentagonal bipyramids, an edgeedge with one CeO7 pentagonal bipyramid, and edges with six ZrO7 pentagonal bipyramids. There are a spread of Zr–O bond distances ranging from 2.05–2.32 Å. In the eleventh Zr4+ site, Zr4+ is bonded to seven O2- atoms to form distorted ZrO7 pentagonal bipyramids that share a cornercorner with one CeO7 pentagonal bipyramid, corners with three ZrO7 pentagonal bipyramids, and edges with seven ZrO7 pentagonal bipyramids. There are a spread of Zr–O bond distances ranging from 2.07–2.28 Å. There are twenty-four inequivalent O2- sites. In the first O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the second O2- site, O2- is bonded in a distorted trigonal non-coplanar geometry to three Zr4+ atoms. In the third O2- site, O2- is bonded in a distorted trigonal non-coplanar geometry to three Zr4+ atoms. In the fourth O2- site, O2- is bonded in a distorted trigonal non-coplanar geometry to one Ce4+ and two Zr4+ atoms. In the fifth O2- site, O2- is bonded in a distorted trigonal non-coplanar geometry to three Zr4+ atoms. In the sixth O2- site, O2- is bonded in a distorted trigonal non-coplanar geometry to three Zr4+ atoms. In the seventh O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ce4+ and two Zr4+ atoms. In the eighth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of distorted corner and edge-sharing OZr4 tetrahedra. In the ninth O2- site, O2- is bonded to one Ce4+ and three Zr4+ atoms to form distorted OCeZr3 tetrahedra that share corners with four OZr4 tetrahedra and edges with four OCeZr3 tetrahedra. In the tenth O2- site, O2- is bonded to one Ce4+ and three Zr4+ atoms to form distorted OCeZr3 tetrahedra that share corners with four OZr4 tetrahedra and edges with four OCeZr3 tetrahedra. In the eleventh O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra. In the twelfth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of distorted corner and edge-sharing OZr4 tetrahedra. In the thirteenth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of distorted corner and edge-sharing OZr4 tetrahedra. In the fourteenth O2- site, O2- is bonded to four Zr4+ atoms to form distorted OZr4 tetrahedra that share corners with four OZr4 tetrahedra and edges with four OCeZr3 tetrahedra. In the fifteenth O2- site, O2- is bonded to one Ce4+ and three Zr4+ atoms to form a mixture of corner and edge-sharing OCeZr3 tetrahedra. In the sixteenth O2- site, O2- is bonded to one Ce4+ and three Zr4+ atoms to form OCeZr3 tetrahedra that share corners with four OZr4 tetrahedra and edges with four OCeZr3 tetrahedra. In the seventeenth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of distorted corner and edge-sharing OZr4 tetrahedra. In the eighteenth O2- site, O2- is bonded in a distorted trigonal non-coplanar geometry to three Zr4+ atoms. In the nineteenth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Ce4+ and two Zr4+ atoms. In the twentieth O2- site, O2- is bonded in a distorted trigonal non-coplanar geometry to three Zr4+ atoms. In the twenty-first O2- site, O2- is bonded in a 3-coordinate geometry to three Zr4+ atoms. In the twenty-second O2- site, O2- is bonded in a distorted trigonal non-coplanar geometry to three Zr4+ atoms. In the twenty-third O2- site, O2- is bonded in a 3-coordinate geometry to three Zr4+ atoms. In the twenty-fourth O2- site, O2- is bonded to four Zr4+ atoms to form a mixture of corner and edge-sharing OZr4 tetrahedra.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-14. Materials Data on CeZr11O24 by Materials Project. https://doi.org/10.17188/1288782

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗