Materials Data on Na4Ti3O8 by Materials Project

Abstract

Na4Ti3O8 crystallizes in the monoclinic C2/m space group. The structure is three-dimensional. there are three inequivalent Na1+ sites. In the first Na1+ site, Na1+ is bonded in a 6-coordinate geometry to six O2- atoms. There are two shorter (2.29 Å) and four longer (2.34 Å) Na–O bond lengths. In the second Na1+ site, Na1+ is bonded to six O2- atoms to form NaO6 octahedra that share corners with six equivalent TiO6 octahedra, edges with four NaO6 octahedra, and edges with four TiO6 octahedra. The corner-sharing octahedra tilt angles range from 11–15°. There are a spread of Na–O bond distances ranging from 2.42–2.52 Å. In the third Na1+ site, Na1+ is bonded to six O2- atoms to form NaO6 octahedra that share edges with four equivalent NaO6 octahedra and edges with six TiO6 octahedra. There are two shorter (2.20 Å) and four longer (2.22 Å) Na–O bond lengths. There are two inequivalent Ti4+ sites. In the first Ti4+ site, Ti4+ is bonded to six O2- atoms to form TiO6 octahedra that share corners with six equivalent NaO6 octahedra, edges with four NaO6 octahedra, and edges with four TiO6 octahedra. The corner-sharing octahedra tilt angles range from 11–15°. There are a spread of Ti–O bond distances ranging from 1.97–2.09 Å. In the second Ti4+ site, Ti4+ is bonded to six O2- atoms to form TiO6 octahedra that share edges with four equivalent TiO6 octahedra and edges with six NaO6 octahedra. There are four shorter (1.96 Å) and two longer (2.06 Å) Ti–O bond lengths. There are three inequivalent O2- sites. In the first O2- site, O2- is bonded to two equivalent Na1+ and three Ti4+ atoms to form ONa2Ti3 square pyramids that share corners with nine ONa3Ti2 square pyramids, edges with four equivalent ONa4Ti2 octahedra, and edges with four equivalent ONa3Ti2 square pyramids. In the second O2- site, O2- is bonded to four Na1+ and two equivalent Ti4+ atoms to form distorted ONa4Ti2 octahedra that share corners with six equivalent ONa4Ti2 octahedra and edges with twelve ONa3Ti2 square pyramids. The corner-sharing octahedral tilt angles are 0°. In the third O2- site, O2- is bonded to three Na1+ and two Ti4+ atoms to form distorted ONa3Ti2 square pyramids that share corners with nine ONa3Ti2 square pyramids, edges with four equivalent ONa4Ti2 octahedra, and edges with four ONa3Ti2 square pyramids.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-22. Materials Data on Na4Ti3O8 by Materials Project. https://doi.org/10.17188/1289501

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗