Materials Data on Li4Nb(TeO4)3 by Materials Project

Abstract

Li4Nb(TeO4)3 is Ilmenite-derived structured and crystallizes in the monoclinic P2 space group. The structure is three-dimensional. there are four inequivalent Li1+ sites. In the first Li1+ site, Li1+ is bonded in a 6-coordinate geometry to six O2- atoms. There are a spread of Li–O bond distances ranging from 1.98–2.62 Å. In the second Li1+ site, Li1+ is bonded in a 6-coordinate geometry to six O2- atoms. There are a spread of Li–O bond distances ranging from 1.98–2.71 Å. In the third Li1+ site, Li1+ is bonded to six O2- atoms to form distorted LiO6 pentagonal pyramids that share corners with six TeO6 octahedra, an edgeedge with one TeO6 octahedra, edges with two equivalent NbO6 octahedra, and faces with two equivalent LiO6 pentagonal pyramids. The corner-sharing octahedra tilt angles range from 40–61°. There are a spread of Li–O bond distances ranging from 2.05–2.36 Å. In the fourth Li1+ site, Li1+ is bonded to six O2- atoms to form distorted LiO6 pentagonal pyramids that share corners with two equivalent TeO6 octahedra, corners with four equivalent NbO6 octahedra, edges with three TeO6 octahedra, and faces with two equivalent LiO6 pentagonal pyramids. The corner-sharing octahedra tilt angles range from 39–61°. There are a spread of Li–O bond distances ranging from 2.01–2.40 Å. Nb4+ is bonded to six O2- atoms to form NbO6 octahedra that share corners with two equivalent TeO6 octahedra, corners with four equivalent LiO6 pentagonal pyramids, edges with two equivalent TeO6 octahedra, and edges with two equivalent LiO6 pentagonal pyramids. The corner-sharing octahedral tilt angles are 46°. There are a spread of Nb–O bond distances ranging from 2.01–2.08 Å. There are three inequivalent Te+5.33+ sites. In the first Te+5.33+ site, Te+5.33+ is bonded to six O2- atoms to form TeO6 octahedra that share corners with two equivalent NbO6 octahedra, corners with four equivalent LiO6 pentagonal pyramids, edges with two equivalent TeO6 octahedra, and edges with two equivalent LiO6 pentagonal pyramids. The corner-sharing octahedral tilt angles are 46°. There is four shorter (1.96 Å) and two longer (1.98 Å) Te–O bond length. In the second Te+5.33+ site, Te+5.33+ is bonded to six O2- atoms to form TeO6 octahedra that share corners with two equivalent TeO6 octahedra, corners with two equivalent LiO6 pentagonal pyramids, edges with two equivalent NbO6 octahedra, and an edgeedge with one LiO6 pentagonal pyramid. The corner-sharing octahedral tilt angles are 52°. There are a spread of Te–O bond distances ranging from 2.02–2.12 Å. In the third Te+5.33+ site, Te+5.33+ is bonded to six O2- atoms to form TeO6 octahedra that share corners with two equivalent TeO6 octahedra, corners with two equivalent LiO6 pentagonal pyramids, edges with two equivalent TeO6 octahedra, and an edgeedge with one LiO6 pentagonal pyramid. The corner-sharing octahedral tilt angles are 52°. There are a spread of Te–O bond distances ranging from 2.16–2.19 Å. There are six inequivalent O2- sites. In the first O2- site, O2- is bonded in a 4-coordinate geometry to two Li1+, one Nb4+, and one Te+5.33+ atom. In the second O2- site, O2- is bonded in a 3-coordinate geometry to two Li1+ and two Te+5.33+ atoms. In the third O2- site, O2- is bonded in a 4-coordinate geometry to two Li1+, one Nb4+, and one Te+5.33+ atom. In the fourth O2- site, O2- is bonded in a 4-coordinate geometry to two Li1+ and two Te+5.33+ atoms. In the fifth O2- site, O2- is bonded to two Li1+, one Nb4+, and one Te+5.33+ atom to form a mixture of distorted edge and corner-sharing OLi2NbTe trigonal pyramids. In the sixth O2- site, O2- is bonded in a 4-coordinate geometry to two Li1+ and two Te+5.33+ atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-02. Materials Data on Li4Nb(TeO4)3 by Materials Project. https://doi.org/10.17188/1290542

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗