Materials Data on Ce6Y2O15 by Materials Project

Abstract

Ce6Y2O15 crystallizes in the monoclinic Cc space group. The structure is three-dimensional. there are six inequivalent Ce4+ sites. In the first Ce4+ site, Ce4+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Ce–O bond distances ranging from 2.30–2.46 Å. In the second Ce4+ site, Ce4+ is bonded to seven O2- atoms to form distorted CeO7 pentagonal bipyramids that share a cornercorner with one CeO7 pentagonal bipyramid, corners with two YO7 pentagonal bipyramids, an edgeedge with one CeO7 pentagonal bipyramid, and edges with two YO7 pentagonal bipyramids. There are a spread of Ce–O bond distances ranging from 2.29–2.34 Å. In the third Ce4+ site, Ce4+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Ce–O bond distances ranging from 2.28–2.52 Å. In the fourth Ce4+ site, Ce4+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Ce–O bond distances ranging from 2.31–2.51 Å. In the fifth Ce4+ site, Ce4+ is bonded to seven O2- atoms to form distorted CeO7 pentagonal bipyramids that share a cornercorner with one CeO7 pentagonal bipyramid, corners with two YO7 pentagonal bipyramids, an edgeedge with one CeO7 pentagonal bipyramid, and edges with two YO7 pentagonal bipyramids. There are a spread of Ce–O bond distances ranging from 2.25–2.37 Å. In the sixth Ce4+ site, Ce4+ is bonded in a body-centered cubic geometry to eight O2- atoms. There are a spread of Ce–O bond distances ranging from 2.30–2.51 Å. There are two inequivalent Y3+ sites. In the first Y3+ site, Y3+ is bonded to seven O2- atoms to form distorted YO7 pentagonal bipyramids that share a cornercorner with one YO7 pentagonal bipyramid, corners with two CeO7 pentagonal bipyramids, an edgeedge with one YO7 pentagonal bipyramid, and edges with two CeO7 pentagonal bipyramids. There are a spread of Y–O bond distances ranging from 2.28–2.41 Å. In the second Y3+ site, Y3+ is bonded to seven O2- atoms to form distorted YO7 pentagonal bipyramids that share a cornercorner with one YO7 pentagonal bipyramid, corners with two CeO7 pentagonal bipyramids, an edgeedge with one YO7 pentagonal bipyramid, and edges with two CeO7 pentagonal bipyramids. There are a spread of Y–O bond distances ranging from 2.26–2.42 Å. There are fifteen inequivalent O2- sites. In the first O2- site, O2- is bonded to three Ce4+ and one Y3+ atom to form OCe3Y tetrahedra that share corners with fourteen OCe3Y tetrahedra and edges with six OCe2Y2 tetrahedra. In the second O2- site, O2- is bonded to three Ce4+ and one Y3+ atom to form OCe3Y tetrahedra that share corners with sixteen OCe3Y tetrahedra and edges with five OCe2Y2 tetrahedra. In the third O2- site, O2- is bonded to three Ce4+ and one Y3+ atom to form a mixture of corner and edge-sharing OCe3Y tetrahedra. In the fourth O2- site, O2- is bonded to two Ce4+ and two Y3+ atoms to form a mixture of corner and edge-sharing OCe2Y2 tetrahedra. In the fifth O2- site, O2- is bonded to four Ce4+ atoms to form a mixture of corner and edge-sharing OCe4 tetrahedra. In the sixth O2- site, O2- is bonded to three Ce4+ and one Y3+ atom to form a mixture of distorted corner and edge-sharing OCe3Y tetrahedra. In the seventh O2- site, O2- is bonded to two Ce4+ and two Y3+ atoms to form a mixture of corner and edge-sharing OCe2Y2 tetrahedra. In the eighth O2- site, O2- is bonded to two Ce4+ and two Y3+ atoms to form a mixture of distorted corner and edge-sharing OCe2Y2 tetrahedra. In the ninth O2- site, O2- is bonded to three Ce4+ and one Y3+ atom to form OCe3Y tetrahedra that share corners with fourteen OCe3Y tetrahedra and edges with six OCe4 tetrahedra. In the tenth O2- site, O2- is bonded to four Ce4+ atoms to form a mixture of corner and edge-sharing OCe4 tetrahedra. In the eleventh O2- site, O2- is bonded to three Ce4+ and one Y3+ atom to form a mixture of corner and edge-sharing OCe3Y tetrahedra. In the twelfth O2- site, O2- is bonded to three Ce4+ and one Y3+ atom to form a mixture of distorted corner and edge-sharing OCe3Y tetrahedra. In the thirteenth O2- site, O2- is bonded to four Ce4+ atoms to form a mixture of corner and edge-sharing OCe4 tetrahedra. In the fourteenth O2- site, O2- is bonded to four Ce4+ atoms to form a mixture of corner and edge-sharing OCe4 tetrahedra. In the fifteenth O2- site, O2- is bonded to three Ce4+ and one Y3+ atom to form a mixture of corner and edge-sharing OCe3Y tetrahedra.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-15. Materials Data on Ce6Y2O15 by Materials Project. https://doi.org/10.17188/1290982

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗